Enhancement of thermal shock resistance in β-Si3N4 coating with in situ synthesized β-Si3N4 nanowires/nanobelts on porous Si3N4 ceramics
A dense β-Si 3 N 4 coating toughened by β-Si 3 N 4 nanowires/nanobelts was prepared by a combined technique involving chemical vapor deposition and reactive melt infiltration to protect porous Si 3 N 4 ceramics in this work. A porous β-Si 3 N 4 nanowires/nanobelts layer was synthesized in situ on porous Si 3 N 4 ceramics by chemical vapor deposition, and then Y–Si–Al–O–N silicate liquid was infiltrated into the porous layer by reactive melt infiltration to form a dense composite coating . The coating consisted of well-dispersion β-Si 3 N 4 nanowires/nanobelts, fine β-Si 3 N 4 particles and small amount of silicate glass . The testing results revealed that as-prepared coating displayed a relatively high fracture toughness, which was up to 7.9 ± 0.05 MPa m 1/2 , and it is of great significance to improve thermal shock resistance of the coating. After thermal cycling for 15 times at ΔT = 1200 °C, the coated porous Si 3 N 4 ceramics still had a high residual strength ratio of 82.2%, and its water absorption increased only to 6.21% from 3.47%. The results will be a solid foundation for the application of the coating in long-period extreme high temperature environment.
危险品化学品经营许可证（带存储）