Microstructural and Optical Properties of Sb2S3 Film Thermally Evaporated from Antimony Pentasulfide and Efficient Planar Solar Cells
Antimony sulfide (Sb 2 S 3 ) thin film is a promising light absorber for solar cell application due to its suitable bandgap, high absorption coefficient, and non-toxic constituents. However, thermally evaporated Sb 2 S 3 thin films experience sulfur loss during evaporation and post-annealing, which do harm to the film quality and the performance of the devices. In this work, for the first time Sb 2 S 3 thin films are prepared by thermally evaporating antimony pentasulfide (Sb 2 S 5 ) precursor. The thermal and microstructural properties of Sb 2 S 3 and Sb 2 S 5 precursors are studied and compared. The crystallization of the Sb 2 S 3 film (S-5) prepared from Sb 2 S 5 precursor is inferior to that (S-3) from Sb 2 S 3 powder. And the annealed S-5 film shows a larger bandgap of 1.69 eV than S-3. However, compared with S-3, planar S-5 thin film solar cells in the configuration of glass/(SnO 2 :F) FTO/TiO 2 /Sb 2 S 3 /Spiro-OMeTAD/Ag exhibit an apparently improved photovoltaic performance, with the best power conversion efficiency of 3.75% and high fill factor of 0.56, which is the highest efficiency of thermally evaporated planar Sb 2 S 3 solar cell. The capacitance–voltage ( C–V ) measurement indicates that this might come from the higher C–V derived space-charge density in S-5. This work offers a new method to prepare Sb 2 S 3 thin films for efficient solar cells.
危险品化学品经营许可证（带存储）