Preparation, mechanical and thermal properties of Si3N4 ceramics by gelcasting using low–toxic DMAA gelling system and gas pressure sintering
In this work, Si 3 N 4 ceramics were fabricated through an aqueous gelcasting method using a low–toxic monomer called N, N–dimethylacrylamide (DMAA) followed by gas pressure sintering at 1850 °C for 2 h under 6 MPa N 2 atmosphere. The effect of solid loading on performance of slurries, green and sintered bodies was investigated systematically. The results show that the slurries with a solid loading as high as 50 vol% (viscosity 0.17 Pa.s at 100 s –1 ) were achieved. With the increase of solid loading (30–50 vol%), the green bodies exhibited a monotonically decreased, however high enough in general, flexural strength of 16.50–11.52 MPa, which was comparable to that of widely–used neurovirulent acrylamide (AM) gelling system. In regard to the sintered bodies, increasing solid loading significantly promoted sintering and improved mechanical properties and thermal conductivity as a result of the increased density, bimodal distribution structure, as well as suitable interfacial bonding strength . The best performance parameters of Si 3 N 4 ceramics, bulk density of 3.25 g/cm 3 , apparent porosity of 0.67%, flexural strength of 898.92 MPa, fracture toughness of 6.42 MPa m 1/2 , Vickers hardness of 2.81 GPa, and thermal conductivity of 34.69 W m –1 K –1 , were obtained at 50 vol% solid loading. This work renders low–toxic DMAA gelling system promising prospect in preparation of high–performance Si 3 N 4 ceramics by gelcasting.
危险品化学品经营许可证（带存储）