The poly(ethylene oxide) based composite solid electrolyte(PEO-CSE) is an effective solution for developing high-performance solid-state lithium battery . However, the poly(ethlene oxide)(PEO) based solid-state lithium battery using 4.0 V cathode suffers from severe interfacial instability problems. In this work, we add additive lithium difluorophosphate(LiPO 2 F 2 ) into the PEO-CSE to form a stable and low resistance interphase at the cathode/electrolyte interface during charge/discharge process. The electrochemical stability window of PEO-CSE increases to ∼5.0 V. Besides, the electrochemical performance of PEO based solid-state lithium battery with LiCoO 2 as cathode is excellent. The discharge capacity of LiCoO 2 /Li cell with LiPO 2 F 2 reaches 108.5 mAh g −1 at 1.0C. In contrast, the discharge capacity that without LiPO 2 F 2 is only 60.0 mAh g −1 . Meanwhile, the PEO-CSE with LiPO 2 F 2 cell delivers stable cycle performance at 4.2 V. The capacity retention maintains 88.5% compared with 16.1%(without LiPO 2 F 2 ) after 100 cycles. Furthermore, it's still maintains 83.3% after 150 cycles. In addition, the cathode/electrolyte interface is analyzed by transmission electron microscope(TEM) and X-ray photoelectron spectroscopy(XPS). Galvanostatic intermittent titration test(GITT) is used to analyze the dynamic diffusion performance. This strategy provides a simple and effective way to improve the high voltage stability of the cathode/electrolyte interface.
A dual-halide solid electrolyte, Li 3 YCl 3 Br 3 , was synthesized using a wet-chemistry route instead of the conventional mechanical ball-milling route. Li 3 YCl 3 B r3 exhibits an ion conductivity of 2.08 mS/cm and an electro- chemical stability window of 3.8 V. Additionally, an all-solid-state lithium-ion battery using Li 3 YCl 3 Br 3 and LiNi 0.83 Co 0.11 Mn 0.06 O 2 (NCM811) as the cathode material achieves a capacity retention of 93% after 200 cycles at 0.3 C and maintains a specific capacity of 115 mA·h/g during 2 C cycling. This exceptional performance is attributed to the high oxidative stability of Li 3 YCl 3 Br 3 and the in-situ formation of Y 2 O 3 inert protective layer on the NCM811 surface under high voltage. Consequently, the study demonstrates the feasibility of a simple, cost-effective wet-chemistry route for synthesizing multi-component halides, highlighting its potential for large-scale production of halide solid electrolytes for practical applications.
危险品化学品经营许可证（带存储）