Polyureas (PU) are well known as a class of high impact engineering materials, and widely used also in emerging advanced applications. As a general observation, most of them are only soluble in a very limited number of highly protonic solvents, which makes their chemical structure analysis a great challenge. Besides the presence of abundant hydrogen bonding, the poor solubility of PU in common organic solvents is often ascribed to the formation of biuret crosslinking in their molecular chains. To clarify the presence of biuret groups in PU has been of great interest. To this end, two samples, based on hexamethylene diisocyanate (HDI) and toluene diisocyanate (TDI) respectively, were synthesized by precipitation polymerization of each of these diisocyanates in water-acetone at 30 °C. Their chemical structures were analyzed by high resolution magic angle spinning (HR-MAS) NMR, and through comparison of their NMR spectra with those of specially prepared biuret-containing polyurea oligomers, it was concluded that biuret group was absent in all the PU prepared at 30 °C. In addition, this NMR analysis was also applied to a PU obtained by copolymerization of TDI with ethylene diamine (EDA) and water at 65 °C in EDA aqueous solution. It was confirmed that biuret unit was also absent in this PU and that EDA was more active than water towards TDI. The presence of EDA was crucial to the formation of uniform PU microspheres. This study provides therefore a reliable method for the analysis of PU chemical structure.
Xubao Jiang,Xiaoli Zhu,Alexandre A. Arnold,Xiang Zheng Kong,Jerome P. Claverie
Owing to the presence of abundant interchain interactions such as hydrogen bonds, polyureas (PU) are only swellable or soluble in a limited number of highly protonic solvents, and the viscosity of the solutions obtained is very high, making their chemical structure characterization hard or even impossible by standard NMR. Accurate structure analysis is also hard by solid-state NMR due to low spectral resolution. The presence of a side reaction in their synthesis generating biuret cross-links is often invoked to explain their insolubility. Here we demonstrate that High Resolution Magic Angle Spinning (HR-MAS) NMR is an efficient tool for the chemical structure analysis even for cross-linked PU. With 1H, 13C, and 1H–15N HSQC combined, a variety of linear and cross-linked PU is analyzed by HR-MAS NMR, and conclusive information on their chemical structure is obtained, which reveals for the first time that the biuret group is absent in all PU.
危险品化学品经营许可证（带存储）