Microstructure and properties of Cr-AlN composite coating prepared by pack-cementation on the surface of Al-containing ODS steel
An Al-containing ODS steel was coated with a composite Cr-AlN layer by pack-cementation treatment. Constituent phases and microstructures of the coating layer were carefully characterized. The results show that the Cr-layer is a Cr-Fe solid solution with {Cr,Fe} 2 N 1-x particles and Cr 2 C particles, while the AlN-layer is composed of AlN particles and α-Fe matrix. The formation of Cr 2 C and {Cr,Fe} 2 N 1-x particles in the Cr-layer is due to the drag effect of the strong carbide-forming element Cr on the carbon in ODS steel and nitridation reaction of NH 4 Cl and Cr, Fe, respectively. During high-temperature pack-cementation, N atoms in the air diffuse into the ODS steel substrate and react with Al in the steel under the catalytic action of yttria , resulting in the formation of the AlN particles. Due to the limited diffusion depth of N and the high nitrogen concentration in the surface layer, the density and size of AlN particles are distributed in a gradient. The particle size is small and high on the side of the Cr-layer, while the particles on the side near the substrate are coarse and low in density. The composite coating greatly improves the surface hardness and friction resistance of the ODS steel.
危险品化学品经营许可证（带存储）