Effect of attached peroxyacid on liquid phase depositional polymerization of EDOT over PI film with adsorbed ferric chloride
To synthesize conducting PEDOT coating on polyimide (PI), hydrolyzed PI film was immersed in H 2 O 2 , FeCl 3 , and EDOT solutions sequentially. The surface compositions of PI after H 2 O 2 immersion were analyzed with XPS and the content of introduced peroxide was determined by iodometry. The content of FeCl 3 adsorbed on PI was evaluated by ash method. The effect of the peroxide and FeCl 3 oxidants on the formation of PEDOT coating and the conductivity of the resultant PEDOT/PI were investigated. In H 2 O 2 solution, carboxylic groups on hydrolyzed PI transformed to peroxyacid groups at magnitude of mmol/m 2 . H 2 O 2 concentration promoted the formation of peroxyacid but depressed the adsorption of FeCl 3 . Attached peroxyacid alone could not initiate the oxidative polymerization of EDOT but could work as secondary oxidant with FeCl 3 together. It enhanced the oxidizing capacity of adsorbed FeCl 3 and led to more conducting PEDOT coating. The sheet resistance of PI film could decrease eight orders of magnitude to 400 Ω/□ after oxidative polymerization in EDOT solution. Without H 2 O 2 treatment, the sheet resistance could be reduced to several kΩ/□ only. The attached peroxyacid enhanced the efficiency of adsorbed FeCl 3 to the formation of conducting PEDOT coating greatly.
危险品化学品经营许可证（带存储）