Surfactant-Mediated Morphological Evolution of MnCo Prussian Blue Structures
In the preparation of nanomaterials, the kinetics and thermodynamics in the reaction can significantly affect the structures and phases of nanocrystals. Therefore, people are keen to adopt various synthetic strategies to accurately assemble the target nanocrystals, and reveal the underlying mechanism of the formation of specific structures. In this work, the total reaction time is adjusted to let the prepared MnCo Prussian blue analogous (MnCoPBA) crystals show four evolving morphological changes at different stages with the assistance of sodium dodecyl sulfate. Furthermore, it is clearly observed that the epitaxial growth along the (100) plane on the shell of MnCoPBA nanocrystals is favored, and the thermodynamics and kinetics in the morphology change process are analyzed in detail. Through the simple pyrolysis, MnCoPBA crystals can be successfully converted into the corresponding carbon composites, of which Mn 2 Co 2 C nanoparticles are evenly distributed in highly graphitized carbon matrix. Among them, PBA-III-700 performs good oxygen reduction reaction performance in alkaline solution with the half-wave potential of 0.801 V and diffusion-limited current density of 5.36 mA cm −2 , and its zinc-air battery exhibits the peak power density of 103.4 mW cm −2 competitive with commercial Pt/C.
危险品化学品经营许可证（带存储）