Surface characteristics of the biomaterials have significant effects on response of osteoblast and formation of new bone tissue. In this study, to improve the bio-performance of polyimide (PI) as an implantable material for bone substitute, concentrated sulfuric acid suspension with tantalum (V) oxide (vTO) submicro-particles of 10w% (PIST10) and 15w% (PIST15) was utilized to modify PI surface. After sulfonation , microporous coatings including vTO particles were created on PI (PIST10 and PIST15) while microporous coating without vTO particles was also created on PI (PIS). Results showed that surface roughness , hydrophilicity and protein adsorption of PIST15 was remarkably higher than PIST10 and PIS. Furthermore, after soaking into simulated body fluid (SBF), no apatite mineralization on PIS was found, while PIST15 with high vTO content exhibited better apatite mineralization compared with PIST10. Moreover, PIS showed low antibacterial property , while PIST15 with high vTO content revealed better antibacterial property compared with PIST10. In addition, cellular response (such as adhesion, proliferation and alkaline phosphatase activity) of bone marrow stromal cells (BMSC) of rat to PIST15 was higher than PIST10 and PIS. In conclusion, the microporous coating of PIST15 including vTO submicro-particles possessed good antibacterial property and bioactivity , which significantly promoted the responses of BMSC. Therefore, PIST15 has potential application prospects for bone substitute.
To improve the antibacterial and osteogenic activities of poly(etherketoneketone) (PEKK), concentrated sulfuric acid (H2SO4) suspension with silicon nitride (SN) microparticle was utilized to modify PEKK surface. Through sulfonation reaction, microporous coatings of PEKK/SN composites were created on PEKK surface, which were integrated with PEKK substrate. The results showed that the content of SN in the microporous coatings increased with the increase of SN content in H2SO4 suspension (PKS without SN, PKSC5 and PKSC10 with 5 and 10 wt % SN content in H2SO4) and that the surface roughness and hydrophilicity of microporous coatings on PEKK were significantly improved with the SN content increasing. In addition, the microporous coating of PKSC10 with high SN content exhibited excellent antibacterial activity due to the synergistic action of the presence of amino (−NH2) and sulfonic acid (−SO3H) groups as well as the improvement of protein absorption. Moreover, the microporous coating of PKSC10 obviously stimulated adhesion, proliferation, and osteogenic differentiation of rat bone mesenchymal stem cells. Furthermore, histological and push-out load evaluation indicated that the microporous coating of PKSC10 significantly promoted osteogenesis and osseointegration in vivo. The results suggested that the microporous coating of PKSC10 with high SN content display good biocompatibility, antibacterial and osteogenic activities, and osseointegration ability, which would have great potential for bone substitutes.
危险品化学品经营许可证（带存储）