The cause of foaming in polishing porcelain stoneware tile residues during sintering: Interface corrosion of Silicate-SiC
The SiO 2 layer preferentially generated on the surface of silicon carbide abrasives in Polishing Porcelain stoneware tile Residues (PPR) is corroded by silicate liquid during firing, resulting in continuous oxidation and foaming of silicon carbide, which makes the PPR difficult to be reused. The PPR is fired to form a silicate liquid that wraps micron silicon carbide in it. In this work, it is possible to study the corrosion of silicate to silicon carbide at high temperature by using two ( Ceramic-SiC ) and three ( Ceramic-SiO 2 -SiC ) layer structure model to simulate the corrosion of silicate to silicon carbide. The corrosion mechanism of SiC in PPR by silicate liquid during firing is revealed that the corrosion rate at its two sides (interfaces) determines the ultimate change in the thickness of the corrosion layer between the ceramic and the SiO 2 layer. Importantly, the corrosion layer thickness with time on the silicate-SiO 2 cross-section periodically presents wave-like changes, which can be attributed to the ionic migration between layers and the rate at which cations cross the corrosion layer when studying the three-layer model.
危险品化学品经营许可证（带存储）