Nanoscale
·
2014
·Vol. 6
·期 11
·5634-5638
·
IF 6.739
Weikuan Duan,Yanyan Zhang,Zhongyue Wang,Jingyi Jiang,Chen Liang,Wei Wei
K5NdLi2F10 nanocrystals were synthesized by a novel synthetic route in the liquid phase, which could improve the morphology and reduce the size effectively, for the first time. The luminescence intensities of the K5NdLi2F10 nanocrystals and their dispersion in polyethylene glycol 400 (PEG-400) approximate to that of neodymium doped phosphate glass (3 mol%), while the lifetimes of the nanocrystals alone and when dispersed with Nd3+ ions (1 × 1020 cm−3) are 303.4 μs and 174.6 μs respectively. Based on the Judd–Ofelt analysis, the emission quantum yield of the dispersion reaches 39.57%. In all, the K5NdLi2F10 nanocrystals and their dispersion have promising applications as liquid laser materials and biological fluorescent markers.
研究领域:
材料科学
·
光学
·
生物标记物
✓ 已验证
产品关联
DOI
PubMed
高影响因子
DIAMOND AND RELATED MATERIALS
·
2023
·
IF 4.1
Mingxia Tian,Guyu Zhang,Xinlei Zhao,Yumin Yan,Jianbo Zhao,Hui Bai,Jianhui Jiang
Herein, Nd-ZnO/g-C 3 N 4 (NZCN) composites were obtained by doping rare-earth element Nd with ZnO using a hydrothermal method , coupled with g-C 3 N 4 (CN) electrostatic ultrasonic self-assembly. The NZCN composite exhibited an impressive methylene blue (MB) removal rate of 94.88 %, with a degradation rate of 0.02637 min −1 after 105 min exposure to 500 W xenon lamp irradiations. Comparatively, the degradation rate of MB by the NZCN composite was five and twice times higher than ZnO and CN samples, respectively. This significant improvement can be attributed to the synergistic effect of Nd, ZnO, and CN, which not only widened the light absorption range but also enhanced the density, separation, and transport of photogenerated electrons (e − ) and holes (h + ), thus improving the photocatalytic performance of the NZCN composites. An in-depth investigation into the photocatalytic reaction process was carried out using free-radical active-species capture experiments, confirming the critical role of h + . Furthermore, the reproducibility and stability of the NZCN composites were assessed over five experimental cycles, demonstrating consistent and stable MB degradation rates of 90.1 % while retaining the crystal structure unchanged. Overall, the construction of rare-earth-metal-doped ZnO and Z-type heterojunctions synergistically improves photocatalytic activity and provides a green and environmentally friendly approach for the removal of organics from wastewater.
研究领域:
材料科学
·
环境科学
✓ 已验证
产品关联
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2013
·
IF 1.789
Xiangbo Ji,Jianguo Deng,Bin Kang,Hui Huang,Xin Wang,Wei Jing,Tao Xu
Dense neodymium-doped yttrium aluminum garnet (Nd:YAG) transparent ceramic was obtained by slip casting and solid-state reaction. The colloidal behavior of the aqueous suspensions of neodymia, yttria , and alumina mixed powders using Dispex A as dispersant was investigated. The variation in zeta potential due to pH alteration was studied. The isoelectric point (IEP) was at pH 4.5 and 4 for the specimens with and without Dispex A, respectively. The optimal dispersion conditions were achieved for the suspensions at pH 9.6 with 0.4 wt% Dispex A. The green body prepared by slip casting was vacuum sintered from 1200 °C to 1750 °C. The grain size of the sintered body increased, and the pore size decreased with increasing sintering temperature . Pore-free Nd:YAG transparent ceramic with a grain size of 5–10 μm was obtained by sintering at 1750 °C for 10 h. The in-line transmittance of the annealed specimen reached 80.8% at 1064 nm.
研究领域:
材料科学
·
光学工程
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF POWER SOURCES
·
2019
·
IF 7.467
Jianqiu Wang,Xu Chen,Shenkun Xie,Lei Chen,Yuan Wang,Jian Meng,Defeng Zhou
We demonstrate the utilization of bismuth tungstate (Bi 2 WO 6 , BW) as a sintering aid and reinforcement component into neodymium-doped ceria (Nd 0.2 Ce 0.8 O 3-δ , NDC) to fabricate bismuth tungstate/neodymium-doped ceria composite electrolyte for intermediate-temperature solid oxide fuel cells (IT-SOFC). The presence of BW lowers the sintering temperature of NDC electrolyte to 1000 °C. Moreover, at 600 °C, the electrical conductivity of 5 mol.% BW-incorporated NDC (5BW-NDC) composite electrolyte is 7.12 times higher than the NDC. It is worth mentioning that the enhanced electrical conductivity of 5BW-NDC composite electrolyte does not include the contribution from electronic conductivity . Furthermore, NDC and 5BW-NDC exhibit excellent compatibility with La 0.6 Sr 0.4 Co 0.8 Fe 0.2 O 3-δ cathode and NiO anode in terms of thermal expansion coefficient and chemical reactivity . The oxygen reduction reaction at 5BW-NDC composite electrolyte/cathode interface is significantly enhanced by ∼40% compared to NDC. Moreover, 5BW-NDC electrolyte-supported SOFC delivers a power density of 0.86 W cm −2 at 700 °C, which is 45.76% higher than the NDC-based SOFC. The output performance remains stable during high-temperature operation for 120 h, which indicates the stability and chemical compatibility of the as-synthesized composite electrolyte with other cell components. The results reveal that BW-NDC composite is a potential electrolyte material for stable and high-performance IT-SOFCs.
研究领域:
材料科学
·
能源工程
✓ 已验证
产品关联
DOI
高影响因子