Electromagnetic absorption materials have gained increasing attention. In this study, we report NiO decorated biomass porous carbon derived from pine nut shells as a promising microwave absorbing material by a facile strategy. The NiO/biomass porous carbon (BPC) is thermally converted from Ni(OH)2/BPC with BPC as the base for precipitation. All products were characterized by XRD, Raman, and SEM techniques, which reveals that the NiO nanoflakes were uniformly self-assembled on the surface of the activated carbon. Compared with counterparts of pure Ni(OH)2 and Ni(OH)2/BPC, a large reflection loss peak of −33.8 dB at 16.4 GHz is achieved for the NiO/BPC composites, and the absorption bandwidth less than −10 dB can reach up to about 6.7 GHz (from 11.3 to 18.0 GHz) with a thickness of 8 mm. The enhanced microwave absorption properties originate from the electric/dielectric polarization and the unique NiO decorated BPC structures. The expanded interfaces, such as NiO–NiO, Ni–BPC and NiO–paraffin interfaces in the complicated porous composites, could boost the interfacial polarization as well as related relaxation which results in enhanced dielectric loss and electromagnetic absorbing properties. In addition, NiO/BPC nanocomposites exhibit comparatively better matching of permittivity and permeability. It is expected that our present investigation could provide a new possibility for biomass based fabrication of potential microwave absorbing materials.
Wang Xiaoyu,Hou Xingyu,Sun Na,Wang Yongqiang,Zhang Yiying,Lv Yuguang,Ding Lixin,Sun Xue
In this work, Waste pine nut shells were used as organic carbon source of biomass to synthesize carbon quantum dots. A highly responsive and selective fluorescent nanosensor (Si-doped biomass-derived carbon dots with molecular imprinted polymers, Si-CDs@MIPs) was designed for determination of Rutin (RT) in Chinese herbal substances like Sophora japonica L. . Not only was the synthesis method simple, environmentally friendly but also can selectively capture and specifically recognize the target compound RT, which was accomplished by a single-step hydrothermal process. The RT content in the real sample is 21%, with a recovery rate ranging from 89.7 to 106.3%, demonstrating excellent reproducibility. The nanosensor can selectively detect RT at a detection limit of 12.5 nmol/L. Therefore, it is showed that Si-CDs@MIPs will be feasible as a sensor for the rapid measurement of RT.
In the current study, an isothermal compression molding process was used to develop enhanced green composites made from alkali-treated pine nut shell particles (TPS) reinforced in fully bio-driven benzoxazine (VB) and epoxy (EP) copolymer. Reinforcement with varying weight percent (wt%) of bio-filler enhanced the properties of composites. Composites showed a rise of 75.9 MPa, 5.8 GPa, and 5.1 kJ/m 2 in flexural strength, modulus, and impact strength, respectively. Thermal stability shows that composites can endure higher temperatures and hence be classified as flame-retardant materials. The dynamic mechanical analysis (DMA) confirms that composites exhibit higher storage modulus, which was elevated to 77.6% compared to the unfilled copolymer. FTIR spectroscopy analyzed the structure of copolymerized composites. Further, finite element analysis (FEA) was observed for the prepared composites. A transversely isotropic composite material model was created with the properties of composites, and stress analysis was observed. FEA outcomes are in good agreement with experimental findings.
危险品化学品经营许可证（带存储）