Bin Sun,Yi Zuo,Jidong Li,Li Wang,Kuangyun Tang,Di Huang,Jingjing Du,Peipei Luo,Yubao Li
Low monomer–polymer conversion is the key factor leading to cytotoxicity for resin-containing restorative materials. This paper provides a new root canal filling system based on self-curing injectable polyurethane which can achieve high conversion in a short time. Traced FTIR spectra show more than 90% NCO group participated in the curing reaction after 4 h, and only about 5% remained after 24 h. The calculated data also testified the curing process supports a third-order reaction, and this efficient and sufficient reaction is postulated to weaken the toxic stimulation. By culturing with L929 murine fibroblasts, the PU sealer is shown to be favorable for cell attachment and proliferation. Then physicochemical properties of the injectable PU-based sealer were evaluated according to the Standard [ISO 6876:2001 (E)] for clinical application. A series of physicochemical properties of PU sealer have been tested comparing with AH Plus and Apexit Plus. And the results present that the self-curing PU sealer could not only match the clinic requirements, but even has better properties than the other two commercial sealers. We expect the high conversion PU sealer has a tremendous potential in the field of root canal filling after further biological evaluation.
A root canal sealer with antibacterial activity can be efficacious in preventing reinfection that results from residual microorganisms and/or the leakage of microorganisms. In the present study, a series of injectable, self-curing polyurethane (PU)-based antibacterial sealers with different concentrations of silver phosphate (Ag3PO4) were fabricated. Subsequently, their physicochemical properties, antibacterial abilities, and preliminary cytocompatibilities were evaluated. The results indicated that the fabricated PU-based sealers can achieve a high conversion rate in a short amount of time. More than 95% of the isocyanate group of PU sealers with 3 wt% (PU3) and 5 wt% (PU5) concentrations of Ag3PO4 were included in the curing reaction after 7 hours. With the exception of those for film thickness for PU5, the results of setting time, film thickness, and solubility were able to meet the requirements of the International Organization for Standardization. The antibacterial tests showed that PU3 and PU5 exhibit stronger antimicrobial effects than that achieved with 1 wt% Ag3PO4 (PU1) and AH Plus (positive control) against Streptococcus mutans. The cytocompatibility evaluation revealed that the PU1 and PU3 sealers possess good cytocompatibility and low cytotoxicity. These results demonstrate that the PU3 sealer offers good physicochemical and antimicrobial properties along with cytocompatibility, which may hold great application potential in the field of root canal fillings.
危险品化学品经营许可证（带存储）