Mild nitridation of perovskite manganite: Synthesis, structure and magnetism
The nitrogen lightly doped perovskite manganite La 0.5 Ba 0.5 MnO (3-δ)-x N x was synthesized following a mild nitridation strategy by optimizing annealing temperature, annealing time and NH 3 /Ar flow rate ratio. Neutron powder diffraction (NPD) characterization evidences an N-doping triggered structural phase transition from pseudo-cubic Pm -3 m to tetragonal P 4/ mmm and further confirms a preferable substitution at O1 and O2 sites closing to the Ba-rich layers. N 1s K-edge X-ray absorption near edge spectrum (XANES) with total fluorescence yield (TFY) mode, X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared (FT-IR) spectroscopy collectively convince the Mn–N bonded state. The O/N atomic ratio is determined to be 2.26/0.22 by XPS analysis closing to the value of 2.25/0.18 from NPD refinement. Magnetic property characterization reveals that both long-range Mn 3+ - O -Mn 4+ ferromagnetic coupling and high Curie temperature ( T C ) are maintained upon N-doping. Besides, significant spin frozen with robust domain pinning is identified below T C which can be ascribed to the short-range Mn–N–Mn clusters and/or oxygen defects. This work expands the connotation of transition-metal based perovskite oxynitride and may inspire the development of photosensitive semiconductor device with magnetic response.
危险品化学品经营许可证（带存储）