Oxygen-regulated spontaneous solid electrolyte interphase enabling ultra-stable solid-state Na metal batteries
Solid-state sodium metal batteries utilizing inorganic solid electrolytes (SEs) hold immense potentials such as intrinsical safety, high energy density, and environmental sustainability. However, the interfacial inhomogeneity/instability at the anode-SE interface usually triggers the penetration of sodium dendrites into the electrolyte, leading to short circuit and battery failure. Herein, confronting with the original nonuniform and high-resistance solid electrolyte interphase (SEI) at the Na-Na 3 Zr 2 Si 2 PO 12 interface, an oxygen-regulated SEI innovative approach is proposed to enhance the cycling stability of anode-SEs interface, through a spontaneous reaction between the metallic sodium (containing trace amounts of oxygen) and the Na 3 Zr 2 Si 2 PO 12 SE. The oxygen-regulated spontaneous SEI is thin, uniform, and kinetically stable to facilitate homogenous interfacial Na + transportation. Benefitting from the optimized SEI, the assembled symmetric cell exhibits an ultra-stable sodium plating/stripping cycle for over 6600 h under a practical capacity of 3 mAh cm −2 . Quasi-solid-state batteries with Na 3 V 2 (PO 4 ) 3 cathode deliver excellent cyclability over 500 cycles at a rate of 0.5 C (1 C = 117 mA cm −2 ) with a high capacity retention of 95.4%. This oxygen-regulated SEI strategy may offer a potential avenue for the future development of high-energy-density solid-state metal batteries.
危险品化学品经营许可证（带存储）