Enhanced thermal conductivity in Si3N4 ceramics prepared by using ZrH2 as an oxygen getter
This work reports the two-step sintering method and thermal conductivity of Si 3 N 4 doped with 1.5 wt% MgO and varied contents of ZrH 2 in the range of 0-5 wt%. The metal hydride reduction reaction in the first step sintering allows the in situ generations of ZrO 2 and the elimination of native SiO 2 . A smaller amount of liquid phase with reduced oxygen content was produced during the second step sintering as a result of the replacement of ZrO 2 by ZrH 2 . With the aid of ZrH 2 as an oxygen getter, the native oxygen in those ZrH 2 -doped samples was removed via a route of SiO 2 →ZrO 2 →SiO(g). Consequently, the densified Si 3 N 4 ceramics with larger volume percent of elongated purified β-Si 3 N 4 grains and less glassy phase were obtained. Ultimately, the optimal thermal conductivity of 116.4 W m −1 K −1 was achieved after sintered at 1900 °C for 12 h by using 3 wt% ZrH 2 and 1.5 wt% MgO as additives.