Sustainable recovery of nickel and aluminum from spent NiAl2O4 catalysts via soda roasting-water leaching: Disruption of NiAl2O4 and leaching kinetic
The widespread use of NiO/Al 2 O 3 catalysts in the petrochemical industry generates hazardous spent materials due to the formation of refractory nickel-aluminum spinel (NiAl 2 O 4 ), which complicates metal recovery and exacerbates resource inefficiency. Traditional direct acid and alkali leaching cannot recover Ni and Al due to excellent stable structure of NiAl 2 O 4 . Here, we propose a simple soda roasting-water leaching strategy to disrupt the spinel lattice and recover Ni and Al with high efficiency. By roasting spent catalysts with Na 2 CO 3 at 1000 °C, Na + ions substituted Al 3+ in the octahedral sites, which destroyed the spinel framework and converted Al 2 O 3 /NiAl 2 O 4 into water-soluble NaAlO 2 . Over 98.31 % of Al was selectively leached at 90 °C, followed by pH-controlled precipitation and calcination at 600 °C to regenerate γ-Al 2 O 3 with the purity of 98.21 %. Residual NiO was recovered via 2 M H 2 SO 4 leaching, with Fe impurities removed through pH-selective precipitation. The kinetic analysis revealed a chemically controlled leaching mechanism ( E a = 47.61 kJ/mol). Final Ni(OH) 2 through calcination at 400 °C yielded reusable NiO. This approach achieved >98 % metal recovery, minimized waste, and aligned with circular economy principles by transforming hazardous spent catalysts into high-purity industrial feedstocks.
危险品化学品经营许可证（带存储）