PHYSICAL CHEMISTRY CHEMICAL PHYSICS
·
2011
·Vol. 13
·期 20
·9232-9237
·
IF 3.454
Jingjie Cui,Dehui Sun,Weijia Zhou,Hong Liu,Peiguang Hu,Na Ren,Haiming Qin,Zhen Huang,Jianjian Lin,Houyi Ma
Two kinds of TiO2 nanobelts were prepared from commercial P-25 powders via an alkaline hydrothermal method with and without an acid etching process. The uncauterized nanobelts (TNs) exhibited a smooth surface, and mixed phases of anatase and TiO2 (B), whereas the cauterized ones (CTNs) displayed a rough surface and a pure anatase structure. TNs and CTNs were then deposited onto a glassy carbon electrode (GCE) surface with a conductive adhesive (CA), and the resulting chemically modified electrodes exhibited electrocatalytic activities in the oxidation of nucleobases in a 0.1 M phosphate buffer solution (PBS) at pH 7.4. For guanine and adenine, well-defined oxidation peaks were observed in voltammetric measurements at about +0.62 and +0.89 V, respectively, at a potential sweep rate of 100 mV s−1, whereas for cytosine, uracil and thymine, the voltammetric features were not obvious. The average surface coverages (Γ) of guanine and adenine on the CTNs/CA/GCE electrode were estimated to be 4.75 × 10−10 and 7.44 × 10−10 mol cm−2, respectively, which were about twice those at the TNs/CA/GCE electrode. The enhanced activity of the CTN-based electrode towards purine nucleobase oxidation was ascribed to the large specific surface area and anatase structures with enhanced (001) facets of the CTN that facilitated adsorption of the analytes onto the electrode surface and charge transport through the electrode surface layer.
研究领域:
分析化学
·
纳米材料科学
·
电化学
·
生物传感
·
分子生物学
·
生物医学工程
✓ 已验证
DOI
高影响因子
JOURNAL OF POWER SOURCES
·
2015
·
IF 6.217
Qin Wang,Yingjun Li,Baocang Liu,Guangran Xu,Geng Zhang,Qi Zhao,Jun Zhang
A series of well-dispersed bimetallic Pd@Pt nanodendrites uniformly supported on XC-72 carbon black are fabricated by using different capping agents. These capping agents are essential for the branched morphology control. However, the surfactant adsorbed on the nanodendrites surface blocks the access of reactant molecules to the active surface sites, and the catalytic activities of these bimetallic nanodendrites are significantly restricted. Herein, a facile reflux procedure to effectively remove the capping agent molecules without significantly affecting their sizes is reported for activating supported nanocatalysts. More significantly, the structure and morphology of the nanodendrites can also be retained, enhancing the numbers of active surface sites, catalytic activity and stability toward methanol and ethanol electro-oxidation reactions. The as-obtained hot water reflux-treated Pd@Pt/C catalyst manifests superior catalytic activity and stability both in terms of surface and mass specific activities, as compared to the untreated catalysts and the commercial Pt/C and Pd/C catalysts. We anticipate that this effective and facile removal method has more general applicability to highly active nanocatalysts prepared with various surfactants, and should lead to improvements in environmental protection and energy production.
研究领域:
纳米催化
·
电化学
·
材料化学
·
能源化学
·
表面科学
·
燃料电池
✓ 已验证
DOI
高影响因子
JOURNAL OF ELECTROANALYTICAL CHEMISTRY
·
2014
·
IF 2.871
Hao Li,Qingni Yu,Bin Yang,Zhongjian Li,Lecheng Lei
Galvanostatic anodic oxidation of artificial human urine (AHU) was carried out by using boron doped diamond (BDD) and IrO 2 electrodes respectively. It was found that organic compounds in urine could be almost completely mineralized in a few hours and ammonia may be oxidized into N 2 by the electro-catalytic process. However, the oxidation processes were highly dependent on the electrode materials. On the non-active BDD electrode complete oxidation occurred, and the final oxidation products of inorganic ions, including ClO 4 − and NO 3 − , were formed. Whereas on the active IrO 2 electrode, the final products generated and left in solution were highly toxic substances, including N 2 H 4 and NO 2 − , because the oxidizing activity on the IrO 2 electrode surface is relatively low. The pH values during the degradation process were monitored and the corresponding degradation mechanisms and pathways on both electrodes are proposed based upon the measured inorganic intermediates.
研究领域:
环境科学
·
电化学
·
水处理技术
·
生物医学工程
·
分析化学
✓ 已验证
DOI
高影响因子
RSC Advances
·
2014
·Vol. 4
·期 86
·46208-46213
·
IF 3.708
Yuqing Lin,Lianglu Hu,Linbo Li,Keqing Wang
This study describes a facile and effective one-pot route to synthesize structurally uniform and electrochemically active nickel hydroxide–graphene nanocomposites (Ni(OH)2–GN) and investigates the electrocatalytic activity toward the oxidation of insulin. Graphene here was used to tether Ni2+ precursor onto surfaces and eventually grow Ni(OH)2 nanoparticles to form hybrid materials. The synthetic Ni(OH)2–GN nanocomposite has a uniform surface distribution, which was characterized with scanning electron microscopy (SEM). Moreover, the composition of synthetic Ni(OH)2–GN nanocomposite was characterized by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FT-IR spectra). The Ni(OH)2–GN were electrochemically treated in 0.1 M NaOH solution through cyclic voltammograms, and then gradually transited into nickel oxyhydroxide–graphene nanocomposites (NiOOH–GN), which demonstrated high catalytic activity and improved stability to insulin oxidation. The steady-state current response increases linearly with insulin concentration from 800 nM to 6400 nM with a fast response time of less than 2 s and a detection limit of 200 nM. The excellent performance of insulin sensor, including long term stability, can be ascribed to the synergistic effects of the large surface area (resulting in high loading ability), dispersing ability and conductivity of graphene and the large surface-to-volume ratio and electrocatalytic activity of Ni(OH)2 nanoparticles.
研究领域:
生物医学工程
·
电化学传感
·
纳米医学
·
糖尿病诊断
·
分子诊断
✓ 已验证
DOI
高影响因子