Limin Liu,Yong Wang,Xiaoliang Zhou,Yixuan Yang,Chao Ma,Yuan Li,Chen Wang,Xiaohong Zhao,Bin Li
A cermet fuel electrode Cu/Ce 0.6 Mn 0.3 Fe 0.1 O 2-δ (Cu/CMF) is proposed for a reversible solid oxide electrochemical cell (SOC) with CO/CO 2 as the shuttle. Cu is inert for the carbon deposition and CMF is electrochemically active for CO oxidation and CO 2 reduction. The electrode polarization resistances in CO at 700, 750 and 800 °C are 0.328, 0.207 and 0.155 Ω cm 2 , respectively, presenting high electrochemical activity towards CO oxidation. The maximal power densities can reach up to 303.3, 482.2 and 691.9 mW/cm 2 at 700, 750 and 800 °C, respectively. When the reversible SOCs are operated in solid oxide electrolysis cell mode, the polarization resistance of the electrolysis cell for pure CO 2 reduction at 800 °C has the minimal value of 0.126 Ω cm 2 at 1.8 V. At 2.0 V, the current densities can reach up to 0.584 1.219 and 2.204 A/cm 2 at 700, 750 and 800 °C, respectively. The durability of the cell in CO for as long as 200 h indicates the electrode has remarkable stability. And the short-term stability characteristics for CO 2 electrolysis at different voltages illustrate that the cell performs well below 2.0 V. The harsh reducing environment at 2.0 V may be detrimental to the Cu/CMF electrode.
We reported a novel Fe 2 O 3 /rutile TiO 2 nanorod (NR) arrays with the heterogeneous structure for photoelectrochemical (PEC) cells, which were fabricated on fluorine-doped tin oxide glass (FTO) substrates that serve as model architecture via a hydrothermal method. Fe 2 O 3 was revealed as an inexpensive and eco-friendly semiconductor sensitizer to make TiO 2 respond to visible light . By using this photoanode, the photoelectric conversion and water splitting properties of PEC cells based on the one-dimensional (1D) Fe 2 O 3 /TiO 2 heterostructures were investigated in detail under simulated sunlight. Meanwhile, the optimization of photovoltaic performance was also achieved by regulating the amount of Fe 2 O 3 . The open circuit voltage and short circuit current of the Fe 2 O 3 /TiO 2 solar cell can reach 0.435 V and 1.840 mA/cm 2 , respectively. In addition, theoretical analysis of the photoelectric effect is preliminarily explored on the basis of the flat band potential results.
危险品化学品经营许可证（带存储）