Enhanced ionic conductivity and lithium dendrite suppression of polymer solid electrolytes by alumina nanorods and interfacial graphite modification
Poor room-temperature ionic conductivity and lithium dendrite formation are the main issues of solid electrolytes. In this work, rod-shaped alumina incorporation and graphite coating were simultaneously applied to poly (propylene carbonate) (PPC)-based polymer solid electrolytes (Wang et al., 2018). The obtained alumina modified solid electrolyte membrane (Al-SE) achieves a high ionic conductivity of 3.48 × 10 −4 S/cm at room temperature with a wide electrochemical window of 4.6 V. The assembled NCM622/Al-SE/Li solid-state battery exhibits initial discharge capacities of 198.2 mAh/g and 177.5 mAh/g at the current density of 0.1 C and 0.5 C, with the remaining capacities of 165.8 mAh/g and 161.3 mAh/g after 100 cycles respectively. The rod-shaped structure of Al 2 O 3 provides fast transport channels for lithium ions and its Lewis acidity promotes the dissociation of lithium salts and release of free lithium ions. The lithiophilic Al 2 O 3 and Graphite form intimate contact with metallic Li and create fast Li + conductive layers of Li-Al-O layer and LiC 6 layer, thus facilitating the uniform deposition of Li and inhibiting Li dendrite formation during long-term cycling. This kind of composite Al-SE is expected to provide a promising alternative for practical application in solid electrolytes.
危险品化学品经营许可证（带存储）