Improving microwave absorption performance of carbonyl iron powder by regulating geometric dimensions and electromagnetic-dielectric synergism
In this study, the microwave absorption performance of carbonyl iron powder (CIP) was enhanced by tuning the geometric dimensions and electromagnetic-dielectric synergism. The ball-shaped CIP was firstly milled into different flattened CIP (FCIP) via a ball milling process with different milling time. The electromagnetic-dielectric synergism of CIP can be regulated by surface coating with silicon dioxide (SiO 2 ) and mixing with multi-walled carbon nanotubes (MWCNT). The minimum reflection loss (RL min ) and effective absorption bandwidth (EAB) values has been greatly improved. Specifically, the maximum EAB and RL min of the FCIP with thick SiO 2 nanoparticle layer are 7.9 GHz at a thickness of 1.9 mm and −40.6 dB at a thickness of 1.7 mm, respectively. For the SiO 2 @FCIP + MWCNT samples, the effective absorption frequency range covers from 3.0 to 18.0 GHz via changing the sample thickness from 1.5 to 5.0 mm. Therefore, this study provide effective strategies to regulate microwave absorption performance of CIP.
危险品化学品经营许可证（带存储）