JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
·
2018
·
IF 3.046
Bang Zhou,Yaqiang Dong,Lei Liu,Liang Chang,Fengqin Bi,Xinmin Wang
The core-shell structured FeSiBCCr@TiO 2 amorphous magnetic powder cores (AMPCs) with excellent comprehensive magnetic properties were successfully prepared using spherical amorphous powders with high quality insulating layer. Scanning electron microscopy, Energy dispersive X-ray spectroscopy analysis, X-ray diffraction, and Fourier transform infrared spectroscopy revealed that the surface of the Fe-based amorphous powders was covered by a continuous amorphous TiO 2 insulation layer. The performances of the AMPCs can be well tuned by changing the thickness of the insulation coating layer, which can be adjusted by controlling the concentration of tetrabutyl titanate (TBOT) in the hydrolysis and condensation reaction system. After annealing at 480 °C for 1 h, the AMPCs with TBOT concentrations of 0.15 ml/g exhibited excellent comprehensive soft magnetic properties, including the highest quality factor of 104.5 at 560 kHz and lowest core loss of 265 mW/cm 3 at f = 100 kHz and B m = 0.05 T. It also maintained a relatively high permeability of 67 up to 5 MHz and superior DC-bias permeability of 68% at a bias field of 100 Oe. This study demonstrated a modified method to develop a novel insulation coating layer to reduce the core loss and improve the magnetic properties of AMPCs.
研究领域:
材料科学
·
磁学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
·
2024
·Vol. 35
·期 7
·1-9
·
IF 2.8
Li Wei,Dai Bo,Li Zhao,Yang Hongwei,Liu Guixiang,Xu Fang
A series of Ni x Zn 1− x Fe 2 O 4 ( NiZn, x = 0.15, 0.25, 0.35, 0.45, 0.65, 0.7, 0.8, 0.85) ferrites were prepared via a solid-phase sintering method. The microstructure, phase, and gyromagnetic properties of the NiZn samples were studied in depth. It was found that the lattice constants, density, and hardness of the samples gradually decreased with increasing Ni 2+ content. X-ray diffraction confirmed that all of the samples were in the spinel phase. Scanning electron microscopy indicated that the grain sizes were more uniformly distributed when x = 0.65. Raman analysis showed that the variation of Ni 2+ content affected the occupancy distribution of ferrite ions. The results indicated that Zn 2+ mainly occupied the A-site and that Ni 2+ mainly occupied the B-site. The coercivity ( H c ) of NiZn increased with increasing Ni 2+ content. Meanwhile, the saturation magnetization ( M s ) initially increased and then decreased. When x = 0.65, the total molecular magnetic moment started decreasing because of the decrease in the net A-site magnetic moment. The sample that had a composition of Ni 0.65 Zn 0.35 Fe 2 O 4 had the highest M s intensity with a value of 78.68 emu/g and a maximum value of 4 πM s = 4780 Gs.
研究领域:
材料科学
·
陶瓷
·
固体物理
·
磁学
✓ 已验证
DOI
高影响因子
JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
·
2020
·Vol. 96
·期 3
·604-613
·
IF 2.008
Fan Lining,Zheng Hui,Zhou Xuehai,Zhang Hongbo,Wu Qiong,Zheng Peng,Zheng Liang,Zhang Yang
In this work, Zn 2 W hexaferrite was prepared by sol–gel (SG) and solid-state reaction (SSR) methods. The dependency of the microstructure, magnetic, and electromagnetic properties of the obtained Zn 2 W hexaferrite on the two different preparation methods and the sintering temperature was investigated. First, single-phase Zn 2 W hexaferrite was obtained by the SG method at sintering temperatures higher than 1250 °C, but this was not the case with the SSR method. Second, the Zn 2 W hexaferrite prepared by the SG method had a larger grain size than those prepared by the SSR method under the same sintering conditions due to the higher activity of the obtained nanosized precursor powder. Third, the saturation magnetization obtained the highest value herein of 77.48 emu/g from the Zn 2 W hexaferrite prepared by the SG method sintered at 1250 °C, which is higher than the value of 72.49 emu/g from the Zn 2 W hexaferrite prepared by the SSR method sintered at 1300 °C. Finally, the values of reflection losses reached a maximum of 22.4 dB at 17.0 GHz with the bandwidth of 0.87 GHz over 10 and 29.5 dB at 17.9 GHz with around the bandwidth of 1.38 GHz for the hexaferrite prepared by the SG method and SSR methods, respectively, which meets the absorption requirement for high-frequency microwave applications.
Influence of the preparation methods of SG and SSR on the properties of prepared Zn 2 W hexaferrites was researched. In virtue of the higher purity and crystal activity, the samples prepared by the SG method had better magnetic properties. In terms of absorption property, the samples prepared by SSR have broader bandwidth and higher values of reflection losses.
研究领域:
材料科学
·
磁学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子
Journal of Superconductivity and Novel Magnetism
·
2024
·
IF 1.6
Pi Siwen,Li Jie,Zhang Yingde,Zhou Weina,Shan Shuo,Zhao Xuan
Ce-substituted M-type Sr 1– x Ce x Fe 12 O 19 ( x = 0.00–0.08) ferrites were successfully synthesized via the ball milling method, and the sintering temperature at 1200 °C for 2 h. The synthesized materials were characterized by X-ray powder diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, field emission scanning electron microscopy (FESEM), and vibrating sample magnetometry (VSM). The elemental makeup of the samples was characterized by energy-dispersive spectrometry (EDS). The XRD results showed the crystal structure and purity of the samples. The FTIR spectroscopy indicated tetrahedral and octahedral tensile vibrations of M-type strontium ferrite at two characteristic peak bands of 554 and 454 cm −1 . The FESEM showed that Ce doping resulted in fine grains. The EDS indicated that Ce content increased with decreasing Sr concentration but that the concentrations of other elements remained basically unchanged. The mass ratio of Sr:Fe is calculated from EDS results and the measured Sr:Fe mass ratio is quite close to the mass ratio calculated from the reactants used to synthesize each sample. The VSM showed that at a Ce doping of x = 0.02, the coercivity of the samples reached the maximum, and the coercivity values and the saturation magnetization were 3878.25 Oe and 73.625 emu/g, respectively. And such high thermal stability further determines that Ce-substituted strontium ferrites have infinite potential in application fields (T = 450.2 °C).
研究领域:
材料科学
·
磁学
✓ 已验证
产品关联
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2024
·
IF 5.1
Chen Zhang,Benzheng Gao,Houyang Yu,Xin Wang,Jianliang Xie
CaO–B 2 O 3 –SiO 2 (CBS) is a promising lightweight, low-dielectric matrix material for high-temperature microwave-absorbing coatings. However, the comprehensive study of absorbent morphology evolution within such coatings and its influence on electromagnetic (EM) performance has not been conducted. In this work, a series of FeSiAl (FSA)/CBS composite coatings with various FSA contents were fabricated using atmospheric plasma spraying. The morphological evolution of the FSA phase and the resulting EM properties of the coatings were systematically analyzed. Experimental findings show that during the spraying process, when the size of FSA clusters in the composite powder exceeds the thickness of CBS splats, FSA clusters form a rigid contact with the underlying solidified coating, leading to the development of a lamellar structure. This lamellar FSA phase creates local conductive networks, which significantly increase the complex permittivity of the coating. These results provide valuable guidance for controlling absorbent morphology and optimizing the EM properties of CBS-based coatings.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
·
2021
·
IF 2.993
Jinxiang Guo,Zhaofei Tong,Qihua Liang,Fangyu Gan,Lepeng Wei,Qingrong Yao,Jianqiu Deng,Zhao Lu,Huaiying Zhou
Bi 1-x Pr x FeO 3 material with perovskite structure was prepared using organic tartaric acid-assisted sol–gel self-propagating combustion method to obtain high-efficiency microwave absorption materials. The influence of the introduction of Pr on dielectric properties and permeability was further studied. After 15% Pr introduced, the lowest reflection absorption loss reaches –32.34 dB, but the absorption bandwidth is only 2.25 GHz. When Pr is 5%, the lowest reflection absorption loss value of −27.31 dB is obtained, and the effective bandwidth which below −10 dB is 3.41 GHz. The structural changes in the process of Pr replacing Bi were analyzed to explore the properties of BPFO perovskite. The influence of strong interaction force, residual magnetization, and natural resonance of ceramic nanoparticles on microwave absorption performance was explored. This work supplies a reliable candidate material for making up electromagnetic attenuation ceramic materials with excellent properties.
研究领域:
材料科学
·
电磁学
✓ 已验证
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE
·
2024
·Vol. 59
·期 15
·6354-6364
·
IF 3.5
Zhu Qijing,Zhang Chaoyun,Peng Xiaoling,Li Jing,Wu Qiong,Xu Jingcai,Hong Bo,Wang Xinqing,Ge Hongliang
Amorphous FeSiB/Al 2 O 3 soft magnetic composites were successfully fabricated in this work by applying an external magnetic field perpendicular or parallel to the magnetic toroidal surface, aiming to investigate the influences of magnetic field orientation on their structures and magnetic properties. The results indicate that amorphous FeSiB particles can form chain-like clusters aligned parallel to the direction of the applied magnetic field, which effectively reduces the magnetic reluctance along this direction. The magnetic toroidal with parallel orientation exhibits the highest effective magnetic permeability of 23.8 and a magnetic loss of 43.693 kW/m 3 at 590 kHz and 10mT, which is superior to both the non-oriented and perpendicularly oriented ones due to its optimized microstructure that reduces magnetic reluctance along the working circuit.
研究领域:
材料科学
·
磁学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF SOLID STATE CHEMISTRY
·
2020
·
IF 2.726
Si-Han Yang,Xiao-Hui Li,Wen-Dong Yao,Qian-Ting Xu,Sheng-Ping Guo
Second-order nonlinear optical (NLO) materials in the middle infrared (MIR) region have attracted widespread interest in view of their importance and deficiency to the laser market’s requirement. Here, we report a new MIR NLO material Eu 8 Sn 4 Se 20 ( 1 ), which represents a new structure type one and the pioneer of the (M II 2 M IV Q 5 ) n (M II = divalent alkali-earth metal, Eu, Yb, Pb, and Sn; M IV = Si, Ge, Sn; Q = S, Se, Te. n = 1, 2, 4) family. It demonstrates obvious second-harmonic generation (SHG) activity. Its optical band gap is determined to be 1.30 eV and its magnetic data exhibits antiferromagnetic-type behavior. Its electronic structure is performed as well.
研究领域:
材料科学
·
物理学
✓ 已验证
DOI
高影响因子
Royal Society Open Science
·
2018
·Vol. 5
·期 2
·
IF 2.504
Wen-Li Qin,Tian Xia,Ying Ye,Ping-Ping Zhang
In this study, the electromagnetic (EM) performance of talc/NiTiO3 composite was evaluated. The morphology of talc displayed a lamella structure; there were many nanoparticles of NiTiO3 coated on the talc lamella. Thermal destruction occurred, which increased the surface area from 2.51 m2 g−1 to 79.09 m2 g−1 at the calcined stage at 650°C. The presence of NiTiO3 increased dielectric loss and magnetic loss of talc. The calculation of EM wave absorption of talc/NiTiO3 obtained a maximum reflection loss of −11.94 dB at the thickness of 6.85 mm; the optimum thickness for microwave absorption is 6.3–7.3 mm. This study revealed a new approach for fabricating an EM absorber and broadening applications of both talc and NiTiO3 in EM absorption.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
APPLIED SURFACE SCIENCE
·
2019
·
IF 5.155
Jun He,Sheng Liu,Lianwen Deng,Dongyong Shan,Can Cao,Heng Luo,Shuoqing Yan
Ti 3 C 2 MXene has demonstrated to be a potential microwave absorber if some difficulties, e.g., poor impedance matching and lack of magnetic loss, can be well-solved. In this paper, laminated Ti 3 C 2 MXene was synthesized using the HF etching method. CoFe 2 O 4 nanoparticles-decorated Ti 3 C 2 MXene (CoFe 2 O 4 -Ti 3 C 2 ) composites were then fabricated via a novel in-situ solvothermal process. The incorporation of CoFe 2 O 4 nanoparticles on the electromagnetic (EM) and microwave absorption properties of Ti 3 C 2 MXene were systematically studied over 2–18 GHz. Interestingly, increased percolation threshold and controlled complex permittivity were well-observed in the CoFe 2 O 4 -Ti 3 C 2 composites. Furthermore, additional magnetic loss due to the existence of magnetic CoFe 2 O 4 was easily obtained. Benefiting from tunable electromagnetic properties, the minimum reflection loss (RL) value of the CoFe 2 O 4 -Ti 3 C 2 -filled absorbing coating achieved −30.9 dB with a matching thickness of only 1.5 mm. A wide effective absorption bandwidth (RL < −10 dB) of 8.5 GHz was correspondingly realized. These results demonstrated that the CoFe 2 O 4 -Ti 3 C 2 composites are favorable as a broadband microwave absorbent.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子
RSC Advances
·
2022
·Vol. 12
·期 16
·9836-9844
·
IF 4.036
Zixu Ma,Beibei Yang,Junjiao Yang
Magnetic materials are being increasingly used in anti-counterfeiting coatings, but the dark colors of magnetic materials greatly limit their applications. This necessitates the development of light-colored magnetic materials. In this study, the heterogeneous precipitation method was used to deposit a layer of titanium dioxide (TiO2) on the surface of magnetic spherical metal particles, followed by the deposition of a layer of Ag by the reduction method, in order to achieve a light color. In the experiment, the particles were initially coated with a few tens of nanometers of TiO2 with a strong shading effect, followed by a further coating of Ag of the same thickness with a similar shading performance. Not only did this achieve a lighter color, but there was no reduction in the magnetic properties of the material after the application of the coating. Scanning electron microscopy (SEM), scanning electron microscopy and energy-dispersive spectroscopy (SEM-EDS), X-ray diffractometry (XRD), and other methods were used to study the changes in morphology and composition before and after the magnetic material was coated. A magnetic tester was used to study the changes in magnetic strength before and after the magnetic material was coated.
研究领域:
材料科学
·
表面化学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
·
2021
·
IF 8.067
Fan Wang,Weihua Gu,Jiabin Chen,Qianqian Huang,Mingyang Han,Gehuan Wang,Guangbin Ji
Perovskite LaCoO 3 is of great potential in electromagnetic wave absorption considering its outstanding dielectric loss as well as the existing magnetic response with the magnetic doping. However, the dissipation mechanism of the magnetic doping on the microwave absorption is lack of sufficient investigated. In this paper, LaCo 1- x Fe x O 3 ( x =0, 0.05, 0.1, 0.15, 0.2, 0.25, 0.3, LCFOs) perovskites with different Fe doping amounts were prepared successfully by the sol-gel method and subsequent heat treatment in the air atmosphere. The structure characterization carried out by the first-principles calculations shows the effect of Fe doping on the dielectric and magnetic properties of LCFOs and the strong hybridization of Co/Fe-3d with O-2p in the LCFOs system was successfully demonstrated. Particularly, when x =0.1 and the thickness is only 1.95 mm, the LaCo 0.9 Fe 0.1 O 3 exhibits the best microwave absorption performance with the minimum reflection loss (RL) value of about -41 dB. The typical samples achieve a broad effective absorption bandwidth (EAB) of 5.16 GHz (7.92-13.08 GHz), which covers the total X band (8-12 GHz). Considering that, the especial Fe doping perovskite is promising to be a candidate as efficient microwave absorbers.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子