Effective immobilization of hexavalent chromium from drinking water by nano-FeOOH coating activated carbon: Adsorption and reduction
In this study, nano α-FeOOH (nFeOOH, 100–500 nm) was coated onto activated carbon (nFeOOH@AC) through a dipping means for enhanced Cr(VI) immobilization from drinking water . The nFeOOH@AC significantly improved the Cr(VI) removal from 19.9% (AC control) to 93.4%. XPS spectra and chromium speciation demonstrated that about 90% of adsorbed Cr(VI) was converted to Cr(III) by the nFeOOH@AC, accompanying with a reduction-oxidation of Fe 3+ /Fe 2+ in the nFeOOH matrix due to electrons delivering between AC and surface-bound Cr(VI). The resultant Cr(III) subsequently reacted with Fe(III) to generate stable (Cr χ Fe 1-χ )(OH) 3 precipitates, leading to a much lower Cr(III) release of 7.5% back to solution by the nFeOOH@AC as compared to the AC control of 33.8%, indicating that the nFeOOH@AC had a prospective potential for Cr(VI) immobilization and decreased Cr residue in treated drinking water. Results from column experiment also showed that the nFeOOH@AC afforded a 3.5 times higher capacity for Cr(VI) immobilization and a 3.4 times longer life-span than the pristine AC. Besides, Cr(VI) immobilization by the nFeOOH@AC was a pH-dependent process and the adsorbed Cr on the nFeOOH@AC could be readily desorbed with acetic acid. The disabled nFeOOH@AC could be refreshed by recoating nFeOOH particles with the above dipping method after stripping all the iron oxides with hydrochloric acid . This study demonstrated that nFeOOH coating is an efficient approach to enhance Cr(VI) elimination by AC during drinking water treatments.
危险品化学品经营许可证（带存储）