Shajie Luo,Fajian Ren,Jiangang Dai,Yan Chen,Zhongzhu Yang
Two kinds of novel poly(arylene ether nitrile)s (CPDP-DCBN and CHDP-DCBN) containing pendant aliphtatic ring were synthesized by 4,4′-cyclopentane-1,1′-diyldiphenol (CPDP) or 4,4′-cyclohexane-1,1′-diyldiphenol (CHDP) and 2,6-dichlorobenzonitrile (DCBN) in this work. The inherent viscosities of poly(arylene ether nitrile)s (PENs) were in the range of 0.701–0.806 dL g−1. The polymers showed high glass transition temperatures (Tg) of 185.4–196.4°C and weight-loss temperatures (T5%) of 447.8–454.3°C. The obtained CPDP-DCBN and CHDP-DCBN could be hot pressed into the films, which showed the tensile strengths of 82.6 MPa and 86.8 MPa, respectively. And the storage modulus of CPDP-DCBN and CHDP-DCBN were about 1.0 GPa and 1.5 GPa at 150°C, respectively. Additionally, the PENs could be dissolved in many solutions at room temperature, such as NMP and concentrated H2SO4, indicating that they had good solubility; they can be processed by the solution method. Meanwhile, the optical transmittance of CPDP-DCBN was 78.1% at 450 nm; it has potential to be applied to the heat-resistant optical film.
Shajie Luo,Junyu Dai,Xiaoyu Ji,Jialin Chen,Yue Jiang,Sixin Li,Tianzi Mao,Xiaoxia Fan
In this work, the monomer N, N′-bis(4-fluorobenzamide)dicyclohexyl methane (BFDCM) was synthesized successfully by 4-fluorobenzoylchloride and 4,4′-diaminodicyclohexylmethane through interfacial reaction, and then the monomer BFDCM and 1,4-benzenediol (HQ) or 4.4′-biphenol (BH) were used to prepare the novel poly(arylene ether amide) (HQ-BFDCM and BH-BFDCM) containing an aliphatic ring in the main chain by nucleophilic substitution in NMP solution. These two polymers exhibited the inherent viscosities ranging from 0.828 to 1.044 dL g−1, high glass-transition temperatures (Tg) of 214.1–235.0 °C, and weight-loss temperature (T5%) of 425.2–441.3 °C. The polymers HQ-BFDCM and BH-BFDCM could completely or partly dissolve in some polar solutions, such as NMP, DMF, and so on, and they showed moderate corrosion resistance. Additionally, the obtained polymers HQ-BFDCM and BH-BFDCM exhibited good optical property, and the optical transmittances of HQ-BFDCM and BH-BFDCM were 74% and 80% at 450 nm, respectively, which showed that they could be applied to the heat-resistant optical films.
危险品化学品经营许可证（带存储）