The heterogeneity of grain refinement and texture formation in conductive copper powder during pulsed electric current sintering have been investigated by means of microstructural analysis of the particle-contacting zone of the samples sintered with micron-sized powders. The particle-contacting region was indicated to experience a higher level of grain refinement than the particle center due to the inhomogeneous temperature distribution among the particle when pulsed electric current passed through. Meanwhile, two main textures of Cube (1 0 0)[0 0 1] texture and Goss (1 1 0)[0 0 1] texture were directly detected in the sintered Cu samples by a combination of electron backscatter diffraction and X-ray diffraction. Based on the experimental results, a feasible mechanism for the formation of texture during the pulsed electric current sintering has been proposed by considering the applied uniaxial pressure and pulsed electric current as well as the rearrangement of grains. In addition, the effects of heterogeneous grain refinement and texture formation on the tensile properties of the sintered Cu samples were also discussed based on the tensile properties and fractographic. These results would contribute to the basic understanding of the sintering mechanisms in pulsed electric current sintering process.
Ti 2 AlN powders were synthesized through molten salt method and re-calcination process using TiH 2 , Al and TiN powders as raw materials at 1100 ℃. The composition of final composite was directly influenced by the initial Al and TiH 2 content in the starting mixture. The purity of the synthesized Ti 2 AlN powder could reach 97.1 wt% when the Al molar ratio was 1.05. Then high strength Ti 2 AlN ceramics were successfully prepared in different modes, including two forms of pulse electric current sintering (PECS/SPS) and hot-pressing sintering (HP). A record-high flexural strength of 719 MPa was obtained for the PECS/SPS with an electrical insulating die (PECS/SPS II) sintered sample, based on the synthesized powder in which the initial molar ratio of Al was 1.1. The sintering behaviors in various modes were analyzed, confirming the shrinkage of particles starting at lower temperature in PECS/SPS II. The density, microstructure, Vickers hardness and elastic modulus of sintered ceramics were also investigated. Therefore, the present work provided the new methods about powder preparation and ceramic sintering of Ti 2 AlN, making it possible to be used as high strength structural ceramics .
危险品化学品经营许可证（带存储）