Orthorhombic Sc 2 Mo 3 O 12 films have been successfully prepared via spin coating technique followed by annealing at 500–750 °C. The phase composition, microstructure, morphology and negative thermal behavior of the synthesized Sc 2 Mo 3 O 12 films were investigated. XRD and XPS analysis indicate that as-deposited film is amorphous . Orthorhombic Sc 2 Mo 3 O 12 films can be prepared after post-annealing at 500–750 °C for 1 h. The crystallinity of Sc 2 Mo 3 O 12 films gradually improved with the increase of post-annealing temperature. SEM analysis shows as-deposited film is smooth and compact, and the grain size of Sc 2 Mo 3 O 12 film grows up as the post-annealing temperature increases. Variable temperature XRD analysis demonstrates that the synthesized orthorhombic Sc 2 Mo 3 O 12 films show stable thermo-chemical and anisotropic NTE property in 25–700 °C. The corresponding coefficients of thermal expansion (CTEs) of the orthorhombic Sc 2 Mo 3 O 12 film in a, b and c directions are −6.68 × 10 −6 °C −1 , 5.08 × 10 −6 °C −1 and −4.76 × 10 −6 °C −1 , respectively. The whole unit cell of the orthorhombic Sc 2 Mo 3 O 12 film shrinks and the volumetric CTE of the Sc 2 Mo 3 O 12 thin film is −6.36 × 10 −6 °C −1 , and the linear CTE is about −2.12 × 10 −6 °C −1 ( α v = 3 α l ).
A novel gold-carbon dots (GCDs) exhibiting relatively high luminescence have been successfully synthesized by a facile solution cast method. Intriguingly, colloidal Au nanoparticles (Au NPs) present an enhancement effect on the photoluminescence of CDs, which can be attributed to the metal enhanced fluorescence (MEF) included two cooperative mechanisms and near-field interactions. Significantly, the 1.5–3 fold enhancement was obtained in the vicinity of Au NPs. The formation mechanism and chemical structure of the as-prepared GCDs were verified by a series of characterization techniques, such as high-resolution transmission electron microscope (HRTEM), Fourier transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The GCDs with optimal fluorescence was acquired by varying volume ratio of colloidal Au NPs to CDs, rendering bright visible light under 460 nm excitation and high quantum yield (QY) of 39%. Given that, a simple spin coating technology was developed for fabricating GCDs film composed of GCDs solution and quartz glass. Subsequently, GCDs-based white light emitting diodes (white LED) was designed through integrating blue LED chips with the yellow light-emitting GCDs film. In addition, the GCDs film at appropriate thickness possesses excellent optical performances with the corresponding optimized color coordinate (CIE) of (0.33, 0.36), the color rendering index (CRI) of 78.2, correlated color temperature (CCT) of 5653 K, and the luminous efficiency (LE) approaching to 43.75 lm W −1 . These superior results demonstrate that GCDs constitute a versatile and effective route for achieving high-performance white LED.
危险品化学品经营许可证（带存储）