Synthesis of lead-free piezoelectric potassium sodium niobates for the preparation of anti-fouling KNN porous membrane
Potassium sodium niobates (KNNs) have garnered significant attention owing to their lead-free nature and potential for use in self-cleaning membranes. This paper presents the synthesis of (K 0.5 Na 0.5 )NbO 3 materials for the fabrication of porous membranes, which enable in situ ultrasonic resonance to effectively eliminate contaminants from the membrane surface . KNN powder was synthesized via solid-state reactions, and the membranes were prepared using conventional sintering techniques. The effects of ball-milling time and calcination temperature on the phase structure, pore size, permeance, flexural strength , chemical stability, and piezoelectric properties were comprehensively investigated. The optimal membranes exhibited an average pore size of approximately 300 nm, a porosity of 23 %, and permeance of 220 L m −2 h −1 bar −1 at a sintering temperature of 1050 °C. A polarized electrical field with a strength of 1 kV/mm was applied to the membranes, resulting in an ultrasonic response of 20 mV at an excitation voltage of 20 V with a frequency of 200 kHz. Furthermore, the in situ anti-fouling performance was evaluated by conducting filtration tests on a 500 ppm oil-in-water (O/W) emulsion, demonstrating that the stationary flux increased by 46.7 % when subjected to an excitation voltage of 60 V.
危险品化学品经营许可证（带存储）