Supercooling suppression and crystallization behaviour of erythritol/expanded graphite as form-stable phase change material
The serious supercooling of erythritol (ET) limits its application in the field of mid-temperature thermal energy storage (TES), especially in the recently developed form-stable phase change materials (PCMs). The primary purpose of this paper is to find out the factors to mitigate the supercooling of ET/expanded graphite (EG) form-stable composite PCM and obtain the correlation among the morphology, kinetic parameters, and a supercooling degree in the non-isothermal crystallization process. Firstly, five types of supercooling relaxation agents (nano-Al 2 O 3 , nano-SiO 2 , CMC, urea, and citric acid) were added to prepare the ET/EG form-stable CPCMs. Among them, the ET/EG/nano-Al 2 O 3 exhibited excellent form-stable ability, a high heat release ratio of 78.9%, and the lowest supercooling degree (Δ T ) of 45.7 °C. Based on the chosen ET/EG/nano-Al 2 O 3 CPCM, the tablet pressures from 1 to 13 MPa were applied, obtaining lowest Δ T decreased by 59.0% in 1 MPa. Moreover, the non-isothermal crystallization processes were discussed on the ET/EG/nano-Al 2 O 3 with the Avrami equation modified by Jeziorny. ET tended to grow spherulites under the high cooling rate of 18 °C/min with triggering as the Johnson-Mehl-Avrami exponent n increased to 4.22. Meanwhile, the supercooling degree increased from 48.8 to 56 °C with the cooling rate growing from 2 to 18 °C/min. And the activity energy Δ E of the ET/EG/nano-Al 2 O 3 CPCM (7092.35 kJ/mol) was smaller than that of the ET/EG CPCM (8211.19 kJ/mol) because of the interaction between the heterogeneous nucleation effect and blocker effect of nano-Al 2 O 3 .
危险品化学品经营许可证（带存储）