JOURNAL OF THE AMERICAN CERAMIC SOCIETY
·
2018
·Vol. 102
·期 5
·2718-2726
·
IF 2.956
Hong Chen,Yao Wang,Jianhui Lin,Minmin Shuai,Haidi Zhu,Wengong Zhang,Qidan Ling
Herein, a novel transparent phenyl vinyl silicone resin nanocomposite containing exfoliated fluorescent Eu-containing hydrotalcite-like compound (EFHSN) is developed to serve as a dual role of color conversion and encapsulation material. Excited by near-NUV light, the EFHSN emits a strong characteristic red light (614 nm). Meanwhile, the EFHSN shows not only excellent transparency ( T > 95%) in the UV-Vis region and high refractive index (1.46) but also superior thermal stability, which could meet the need of commercial encapsulation materials and optical application. Therefore, the EFHSN is expected to be used in InGaN-based NUV light-emitting diodes and flexible optoelectronic device.
研究领域:
材料科学
·
光学工程
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF LUMINESCENCE
·
2023
·
IF 3.6
Jiawen Li,Jiawen Wang,Feifei Huang,Youjie Hua,Shiqing Xu,Ruoshan Lei
In pursuit of healthy lighting, the exploitation of high-quality Eu 2+ -activated phosphors available for near-ultraviolet light-emitting diode (NUV-LED) chip-based white LED (WLED) has fetched growing interest. Herein, a novel NUV-light excitable Rb 3 GdSi 2 O 7 : Eu 2+ phosphor is successfully synthesized via a high-temperature solid-state reaction method. The crystal structure of Rb 3 GdSi 2 O 7 is found to be hexagonal, belonging to space group P6 3 /mmc. The Rb 3 GdSi 2 O 7 : Eu 2+ phosphor exhibits a broad excitation band in the 300–450 nm wavelength range, and it emits strong yellow-green light with peak at 543 nm upon 365 nm excitation. Benefitting from the high structure rigidity of host matrix, Rb 3 GdSi 2 O 7 : Eu 2+ also possesses a desired luminescence thermal stability (423 K, 85.6%). The WLED device fabricated using a 365 nm chip and a blend of the as-prepared Rb 3 GdSi 2 O 7 : Eu 2+ yellow-green phosphor and commercial BaMgAl 10 O 17 : Eu 2+ blue phosphor displays an excellent color-rendering index of 95.9 at a low correlated color temperature of 4373 K. This work confirms the applicative potential of Rb 3 GdSi 2 O 7 : Eu 2+ in NUV-converted warm WLEDs, which may promote the development of high-color-quality healthy lighting.
研究领域:
材料科学
·
光学工程
✓ 已验证
产品关联
DOI
高影响因子
DALTON TRANSACTIONS
·
2023
·Vol. 53
·期 3
·996-1003
·
IF 4
Qiang Zhang,Xin Ding,Bin Liu,Yuhua Wang
The development of novel phosphors with excellent luminescence properties for white light-emitting diodes (WLEDs) is always a formidable task. Compared with the traditional laborious and aimless “trial and error” experiments, a mineral-inspired prototype strategy can provide an efficient and accurate method. Herein, for the first time, a novel yellow-emitting phosphor NaBaY2(PO4)3:Eu2+ was discovered using the mineral-inspired prototype strategy and cation substitution method. The phosphor was prepared via the high-temperature solid-state reaction method, and its crystal structure, luminescence properties and potential application for WLEDs were systematically investigated. The NaBaY2(PO4)3 phase was derived from the K2Mg2(SO4)3-type mineral structure and a photoluminescence study revealed that the phosphor can emit bright yellow light with a maximum at 545 nm upon excitation at 351 nm. A WLED lamp was fabricated by the use of a blend of commercial blue-emitting BaMgAl10O17:Eu2+, yellow-emitting NaBaY2(PO4)3:Eu2+ and red-emitting (Ca, Sr)AlSiN3:Eu2+ phosphors with a 380 nm LED chip. The CIE, CCT, Ra and efficiency of the as-fabricated LEDs were measured to be equal to (0.366, 0.365), 4327 K, 91.2 and 40.8 lm W−1, respectively. These results suggest that NaBaY2(PO4)3:Eu2+ could be a promising candidate for n-UV WLEDs.
研究领域:
材料科学
·
无机化学
·
光电子学
·
半导体照明
·
发光材料
✓ 已验证
DOI
高影响因子
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
·
2020
·Vol. 126
·期 9
·711
·
IF 1.81
Liu Dong,Jin Yahong,Xiong Guangting,Lv Yang,Wu Haoyi,Ju Guifang,Chen Li,Hu Zhengfa,Hu Yihua
A series of broadband blue-green phosphors Rb 0.5+ y Na 1.5− y (Li 3 SiO 4 ) 2 : x Eu 2+ (0 ≤ y ≤ 0.4, 0.01 ≤ x ≤ 0.08) were synthesized by the high-temperature solid-state reaction. The powder X-ray diffraction was employed to explore the crystal structural evolution from RbNa 3 (Li 3 SiO 4 ) 4 to RbNa(Li 3 SiO 4 ) 2 with the increasing of Rb + . The spectra show the optimized composition was determined as y = 0.4. The luminescence, lifetime decay curves and thermal steadily spectra of Rb 0.9 Na 1.1 (Li 3 SiO 4 ) 2 : x Eu 2+ phosphors were investigated in detail. The phosphor of Rb 0.9 Na 1.1 (Li 3 SiO 4 ) 2 :Eu 2+ shows suitable visible spectra (450–550 nm, cover the blue and green regions), excellent thermal quenching (104%@150 °C of the initial integrated intensity at room temperature under 396 nm excitation) and broad excitation spectrum (320–450 nm). Finally, a commercial near-UV LED devices (395 nm) were fabricated with the Rb 0.9 Na 1.1 (Li 3 SiO 4 ) 2 :Eu 2+ phosphor as blue-green and commercial red phosphor CaAlSiN 3 :Eu 2+ with a warm color temperature of 3104 K and a color rendering index of 91.8. This result indicated that Rb 0.9 Na 1.1 (Li 3 SiO 4 ) 2 :Eu 2+ may be a promising blue-green phosphor for indoor lighting.
研究领域:
材料科学
·
发光材料
·
固体化学
·
照明技术
·
无机化学
✓ 已验证
DOI
高影响因子