Calcium vacancy enhanced self-reduction of Ce4+ for single-phase full-spectrum lighting and information encryption
Due to the wide and adjustable emission range, Ce 3+ is an indispensable luminous center for full spectrum lighting. However, it needs to be sintered at high temperature in a reducing atmosphere, resulting in difficulty to coexisting with other multivalent activated ions (such as Eu 3+ , Tm 3+ ), which greatly hinders the formation of full spectrum. In this study, a calcium vacancy enhanced self-reduction of Ce 4+ is realized in CaNaSb 2 O 6 F (CNSOF) host under air atmosphere sintering, through which Ce 3+ , Tm 3+ and Eu 3+ coexisting in a single-phase full spectrum phosphor was prepared. Notably, the artificial introduction of a calcium vacancy was designed to verify this self-reduction mechanism. Moreover, the energy transfer kinetics among Tm 3+ , Ce 3+ and Eu 3+ were explored. Finally, combined with a 340 nm UV chip, a full spectrum phosphor-converted light-emitting diode (pc-LED) was fabricated, showing a broad emission range from 400 to 750 nm, Commission Internationale de I’Eclairage (CIE) of (0.3485, 0.3673), Ra of 92 and correlated color temperature (CCT) of 4933 K. Utilizing the variation in emission colors of this phosphor under different UV wavelengths, a dual encryption method combining point character code and fluorescent encryption technique is proposed. This work provides an effective path for Ce 4+ self-reduction to apply in full spectrum pc-LED and information encryption.
危险品化学品经营许可证（带存储）