Carbonation of argon oxygen decarburization stainless steel slag and its effect on chromium leachability
This study focuses on evaluating the carbonation potential of argon oxygen decarburization (AOD) slag and analyzing influence mechanism of carbonation on chromium leachability . Static thin-film accelerated carbonation and sequential leaching tests were carried out. Results show that the liquid to solid (L/S) ratio was the most influencing factor for AOD slag’s carbonation, and the maximum carbonation ratio of AOD slag was 50–52% (L/S = 0.4 mL/g, P CO2 = 7.5 bar, and t > 6 h). Dicalcium silicate’s carbonation resulted in the generation of amorphous calcium carbonate , crystalline calcite and silica gel . AOD slag’s smooth surface could be eroded by these products gradually with carbonation furthered. The mineral phase evolution clearly influenced the mineral phase hydrolysis and physical encapsulation, and thus affected the hydrolysis behavior of the primary phase and the generation behavior of the secondary phase in the carbonated slags. Chromium leachability (20 days) declined to its lowest value (1.7 mg/kg) as the carbonation ratio growing to 23% and then increased to its highest value (7.9 mg/kg) with the carbonation ratio increasing to 52%. Chromium leachability varies with the carbonation ratio. The optimal carbonation ratio that resulting in minimum chromium leaching risk must be taken full in mind before using AOD slag in carbonation-related production activities.
危险品化学品经营许可证（带存储）