Ting Bai,Xiaohui Li,Liang Ding,Jin Wang,Yong-Shan Xiao,Bin Cao
A series of Zn-modified HBeta (Zn/HBeta) catalysts were prepared via the wetness impregnation method with different zinc precursors such as ZnSO4·7H2O, ZnCl2, C4H6O4Zn·2H2O and Zn(NO3)2·6H2O, and their catalytic performance in the conversion of ethanol to propylene reaction was evaluated. Results indicate that the amount and strength distribution of the acid sites of the Zn/HBeta catalysts were easily tuned by employing different types of zinc precursors. More importantly, when the zinc species were introduced to the HBeta, the propylene yield was significantly enhanced, whereas the yields of ethylene and C2–C4alkanes were remarkably suppressed. For the catalyst prepared by using the ZnCl2precursor, a higher propylene yield of up to 43.4% for Zn/HBeta-C was achieved as a result of the moderate amount and strength distribution of acid sites. The average coking rate of the used Zn/HBeta catalysts strongly depended on the amount of total acid sites, especially the strong acid sites, i.e., the higher the amount of total acid sites of the catalyst, the greater the average coking rate. For the catalyst prepared by using the ZnSO4·7H2O precursor, Zn/HBeta-S exhibited a better stability even after depositing more coke, which was due to the higher amount of strong acid sites.
Zinc selenide (ZnSe) nanocrystals were synthesized via a phosphine-free route using the highly reactive alkylamine-H 2 Se complex as selenium precursor and zinc precursors with different reactivity. The reactivity of zinc precursor was tuned by using three kinds of zinc carboxylates with different alkyl chain lengths, including zinc acetate, zinc nonanoate, and zinc stearate. The effect of the reactivity and the amount of zinc precursor on nucleation and growth of ZnSe nanocrystals were investigated by ultraviolet-visible absorption and photoluminescence spectra. Result indicates that the growth and optical property of the resulting ZnSe nanocrystals are strongly dependent on the alkyl chain length and the amount of the zinc carboxylates and both shorter alkyl chain length, and more amount of zinc carboxylate will lead to faster growth of ZnSe nanocrystals. This allows that the controlled growth and excellent optical property of high-quality ZnSe nanocrystals can be achieved by combining the different reactivity and the used amount of zinc precursor, such as by using stoichiometric and reactive Zn precursor and Se precursor or by using larger amount of more unreactive Zn precursor relative to the highly reactive alkylamine-H 2 Se complex precursor.
危险品化学品经营许可证（带存储）