Tire wear particles (TWPs) are considered an important component of microplastic pollution in the marine environment and occur together with a variety of aquatic pollutants, including frequently detected bisphenols. The adverse effects of TWPs or bisphenols on aquatic organisms have been widely reported. However, the combined toxicity of TWPs and bisphenols is still unknown. In this study, the combined toxicity of both pristine (p-) and aged TWPs (a-TWPs) and four bisphenols ((bisphenol A (BPA), bisphenol F (BPF), bisphenol S (BPS), and bisphenol AF (BPAF)) to Tigriopus japonicus was evaluated. TWPs increased the toxicity of BPA and BPF but decreased the toxicity of BPAF. For BPS, there was synergistic toxic effect in the presence of p -TWPs, but slightly antagonistic effect was observed in the presence of a-TWPs. This adsorption of BPAF by TWPs resulted in a reduction of its toxicity to the copepod . A-TWPs could release more Zn than p -TWPs, and the released Zn contributed to the synergistic effect of TWPs and BPA or BPF. The aggregation formed by TWPs in certain sizes (e.g., 90–110 μm) could cause intestinal damage and lipid peroxidation in T. japonicus . The synergistic effect of p -TWPs and BPS might be due to the aggregation size of the binary mixture. The results of the current study will be important to understand the combined toxic effect of TWPs and bisphenols and the potential toxic mechanisms of the binary mixture.
Qiming Luo,Huiliang Cao,Lanyu Wang,Xiaohan Ma,Xuanyong Liu
Cell-selective toxic titanium is highly desired in clinical dental practice. Herein, based on the in situ conversion of ZnO to ZnO@ZnS, nanorod-array structured coatings with a controllable release features of zinc (Zn), has been successfully fabricated by a two-step hydrothermal method to endow titanium surface with cell-selectivity, i.e. boosting the functions (attachment and migration) of human gingival fibroblasts (HGnFs) while acting against the invasion of pathogenic bacteria. The improved functions of HGnFs over the ZnO@ZnS nanorod-array were attributed to the material’s optimized zinc release, which was decreased from an order of 3.5 mg L −1 to about 0.3 mg L −1 (within the first week). But more importantly, this concentration still had a high antibacterial efficacy up to 100% (against both the S. aureus and E. coli , 10 7 CFU mL −1 ). This study demonstrated that a ZnO@ZnS nanorod-array coating could be a promising strategy to endow titanium dental implants with improved soft tissue sealing and effectively reduce peri-implantitis.
危险品化学品经营许可证（带存储）