The massive stockpiling of electrolytic manganese residue (EMR) has caused serious environmental pollution. In this study, EMR, coal gangue (CG), and fly ash (FA) were used as raw materials to obtain the optimal mix ratio based on Design-Expert mixture design. The effects of activator modulus, liquid–solid (L/S) ratio, and curing temperature on the mechanical properties of geopolymers were investigated. The results showed that the compressive strength of the prepared geopolymer was 12.0 MPa, and the 28d leaching of Mn was 0.123 mg/L under the conditions of EMR:CG:FA = 0.43:0.34:0.23, L/S = 0.9, a curing temperature of 60 °C, and a curing time of 24 h. This indicates that the geopolymer is an environmentally friendly material with high compressive strength. The mineral composition of the geopolymer is mainly hydrated calcium silicate and geopolymer gel. In addition, a more stable new mineral phase, MnSiO3, was generated. The Fourier transform infrared (FTIR) spectrogram showed that the peak at 1100 m−1was shifted to 1112 cm−1, which indicated that a geopolymerization reaction had occurred. Through scanning electron microscopy (SEM) and energy dispersive spectrum (EDS) analysis, it was identified that the geopolymerization produced a large amount of amorphous gelatinous substances with a relatively dense structure, the major elements being oxygen, silicon, aluminum, calcium, and sodium.
Wenchao Zhang,Lu Shen,Ruyue Xu,Xue Dong,Shurui Luo,Huajie Gu,Fenju Qin,Hengwei Liu
Microbially induced carbonate precipitation (MICP), as an eco-friendly and promising technology that can transform free metal ions into stable precipitation, has been extensively used in remediation of heavy metal contamination. However, its depressed efficiency of heavy metal elimination remains in question due to the inhibition effect of heavy metal toxicity on bacterial activity. In this work, an efficient, low-cost manganese (Mn) elimination strategy by coupling MICP with chitosan biopolymer as an additive with reduced treatment time was suggested, optimized, and implemented. The influences of chitosan at different concentrations (0.01, 0.05, 0.10, 0.15 and 0.30 %, w/v) on bacterial growth, enzyme activity, Mn removal efficiency and microstructure properties of the resulting precipitation were investigated. Results showed that Mn content was reduced by 94.5 % within 12 h with 0.15 % chitosan addition through adsorption and biomineralization as MnCO 3 (at an initial Mn concentration of 3 mM), demonstrating a two-thirds decrease in remediation time compared to the chitosan-absent system, whereas maximum urease activity increased by ∼50 %. Microstructure analyses indicated that the mineralized precipitates were spherical-shaped MnCO 3 , and a smaller size and more uniform distribution of MnCO 3 is obtained by the regulation of abundant amino and hydroxyl groups in chitosan. These results demonstrate that chitosan accelerates nucleation and tunes the growth of MnCO 3 by providing nucleation sites for mineral formation and alleviating the toxicity of metal ions, which has the potential to upgrade MICP process in a sustainable and effective manner. This work provides a reference for further understanding of the biomineralization regulation mechanism, and gives a new perspective into the application of biopolymer-intensified strategies of MICP technology in heavy metal contamination.
危险品化学品经营许可证（带存储）