Wenfei Shen,Chunpeng Yang,Xichang Bao,Liang Sun,Ning Wang,Jianguo Tang,Weichao Chen,Renqiang Yang
A simple, solution-processed ultrathin CuO X anode buffer layer was fabricated for high performance organic solar cells (OSCs). XPS measurement demonstrated that the CuO X was the composite of CuO and Cu 2 O. The CuO X modified ITO glass exhibit a better surface contact with the active layer. The photovoltaic performance of the devices with CuO X layer was optimized by varying the thickness of CuO X films through changing solution concentration. With P3HT:PC 61 BM as the active layer, we demonstrated an enhanced PCE of 4.14% with CuO X anode buffer layer, compared with that of PEDOT:PSS layer. The CuO X layer also exhibits efficient photovoltaic performance in devices with PBDTTT-C:PC 71 BM as the active layer. The long-term stability of CuO X device is better than that of PEDOT:PSS device. The results indicate that the easy solution-processed CuO X film can act as an efficient anode buffer layer for high-efficiency OSCs.
Ran Ji,Ding Zheng,Chang Zhou,Jiang Cheng,Junsheng Yu,Lu Li
Tungsten oxide (WO3) is prepared by a low-temperature ultrasonic spray pyrolysis method in air atmosphere, and it is used as an anode buffer layer (ABL) for organic solar cells (OSCs). The properties of the WO3transition metal oxide material as well as the mechanism of ultrasonic spray pyrolysis processes are investigated. The results show that the ultrasonic spray pyrolysized WO3ABL exhibits low roughness, matched energy level, and high conductivity, which results in high charge transport efficiency and suppressive recombination in OSCs. As a result, compared to the OSCs based on vacuum thermal evaporated WO3, a higher power conversion efficiency of 3.63% is reached with low-temperature ultrasonic spray pyrolysized WO3ABL. Furthermore, the mostly spray-coated OSCs with large area was fabricated, which has a power conversion efficiency of ~1%. This work significantly enhances our understanding of the preparation and application of low temperature-processed WO3, and highlights the potential of large area, all spray coated OSCs for sustainable commercial fabrication.Keywords:tungsten oxide;anode buffer layer;organic solar cells;large area;ultrasonic spray pyrolysis method
危险品化学品经营许可证（带存储）