Tobermorite and Al-substituted tobermorite with varying Al/(Si + Al) molar ratios were synthesized via the static hydrothermal method. The effect of different Al substitution ratios on the structure of tobermorite was investigated by XRD, SEM–EDS, TG–DSC, FT–IR,29Si, and27Al MAS–NMR. The interplanar crystal spacing of (002) increased with the increment of the Al substitution ratio. The maximum ratio of the Al substitution for Si in the structure of tobermorite was about 15 at %, which was limited by the compositions of tobermorite and the electrostatic repulsive forces caused by Al substitution. The DSC curve of the tobermorite with an Al/(Al + Si) molar ratio of 0.15 showed a larger exothermic peak area at 850 °C, indicating that the Al-O-Si bond was formed in the structure of tobermorite and the Al participated in the recrystallization. The29Si and27Al MAS–NMR results confirmed that tetrahedral Al was introduced into the structure of the tobermorite. New silicon sites, Q2(1Al) and Q3(1Al), formed by the Al substitution for Si in bridging and non-bridging sites, were detected. Compared to the tobermorite without Al substitution, the adsorption capacity of Al-substituted tobermorite with Al/(Al + Si) = 0.15 to Na+was improved by 44%.Keywords:hydrothermal synthesis;Al-substituted tobermorite;29Si MAS–NMR;27Al MAS–NMR;adsorption capacity
A series of novel hierarchical ZSM-5 zeolite membranes with tunable mesopore sizes have been prepared successfully by using amphiphilic organosilane 3-[(trimethoxysilyl) propyl]octyldimethyl-ammonium chloride (TPOAC) as the mesogenous template and part of the Si source. The effects of several synthesis parameters, such as the TPOAC/SiO 2 ratio, synthesis temperature and crystallization time, on the microstructures and rejection performance of the hierarchical ZSM-5 zeolite membranes were systematically investigated. Multiple techniques, such as XRD , SEM, N 2 adsorption techniques, TEM, IR, 13 C MAS NMR and 29 Si MAS NMR were employed for the characterizations. The filtration of dextran in water shows that the membranes have molecular weight cutoff (MWCO) ranging from 9500 to 943,000, corresponding to the molecular size in the range of 4.5–37 nm. The sharp increase in the rejection of dextran with the increase of molecular weight indicated narrow pore size distribution of the membrane. These results show that the hierarchical mesoporous ZSM-5 zeolite membranes have a great potential for ultrafiltration with high performance.
危险品化学品经营许可证（带存储）