Anion exchange membrane water electrolysis (AEMWE) is one of the most promising technologies for producing green hydrogen; however, they still suffer from durability issues. One task is to find suitable electrolyte conditions for anode catalysts that endow them with both high activity and stability. Herein, we benchmark the pH–stability relationship of four typical metal oxides as anode catalysts in the AEMWE. Their electrochemical performance and structural stability were in-depth analyzed through impedance, dissolved composition in the electrolyte, and correlated Pourbaix diagram. NiFe2O4 with the best activity and stability in the strong alkaline (pH = 14) shows terrible stability in pure water, which is then verified due to the severe Fe leaching, and it cannot be alleviated by alkaline pre-activation. Notably, Co3O4 shows comparable activity and stability to IrO2 in pure water and weak alkaline conditions. At pH = 12, it entails only ∼2.18 V to reach 1.0 A cm–2 and stabilizes for 40 h, being superior to others. This work screens out suitable transition metal oxides as a substitute for noble metals and their optimal application scenarios for AEMWE.
The development of an efficient and durable oxygen evolution reaction (OER) electrode is needed to solve the bottleneck in the application of an anion exchange membrane water electrolyzer (AEMWE). In this work, the self-supporting NiFe layered double hydroxides (NiFe LDHs) “nanoflower” cluster OER electrode directly grown on the surface of nickel fiber felt (Ni fiber) was synthesized by a one-step impregnation at ambient pressure and temperature. The self-supporting NiFe LDHs/Ni fiber electrode showed excellent activity and stability in a three-electrode system and as the anode of AEMWE. In a three-electrode system, the NiFe LDHs/Ni fiber electrode showed excellent OER performance with an overpotential of 208 mV at a current density of 10 mA cm−2in 1 M KOH. The NiFe LDHs/Ni fiber electrode was used as the anode of the AEMWE, showing high cell performance with a current density of 0.5 A cm−2at 1.68 V and a stability test for 200 h in 1 M KOH at 70 °C. The electrocatalytic performance of NiFe LDHs/Ni fiber electrode is due to the special morphological structure of “nanoflower” cluster petals stretching outward to produce the “tip effect,” which is beneficial for the exposure of active sites at the edge and mass transfer under high current density. The experimental results show that the NiFe LDHs/Ni fiber electrode synthesized by the one-step impregnation method has the advantages of good activity and low cost, and it is promising for industrial application.Keywords:NiFe layered double hydroxides (NiFe LDHs);oxygen evolution reaction (OER);anion exchange membrane water electrolyzer (AEMWE)
危险品化学品经营许可证（带存储）