In this work, we have synthesized hexapods AgCl crystals with mace pods for the first time. Diallyldimethylammonium chloride (DDA)-controlled stepwise evolution of AgCl crystals from octahedron to hexapods with mace pods are achieved by one-pot method. The intermediates have been captured which show the basic process of crystal growth. In this process, octahedra AgCl crystals firstly grow along the <100> direction and then change to grow in the <110> direction. At the same time, the size of AgCl grow from 2 μm to 20 μm. Due to the poor absorption of visible light by AgCl, sodium borohydride(NaBH4) is used to reduce AgCl hexapods with mace pods crystals. By changing the mole ratio(R) of NaBH4to AgCl, the new structure was reduced to obtain a series of Ag@AgCl microstructures. Visible light catalysis effects of the Ag@AgCl microstructures on degradation of methyl orange (MO) were investigated. The Ag@AgCl microstructures with R = 0.02 have a high photocatalytic performance, which completely degrades MO in 40 min.Keywords:hexapod AgCl;one-pot method;Ag@AgCl microstructure;MO degradation
Controllable morphological metal catalytic materials have always been a focus in research. In the previous work, hexapod AgCl was successfully synthesized. In this paper, hexapod Ag@AgCl microstructures with diverse Ag contents are prepared through NaBH4reduction. They are characterized by scanning electron microscopy (SEM) and the element distribution is proved by an energy dispersive X-ray spectrometer (EDS). They are porous dendritic microstructures with a large specific surface area and a rough surface, which display high catalytic performance and surface-enhanced Raman spectroscopy (SERS) activity. Furthermore, the hexapod Ag@AgCl microstructure is devoted as a dual catalyst to monitor the reduction of 4-nitrothiophenol (4-NTP) to 4-aminothiophenol (4-ATP) in situ using SERS. Ultraviolet–visible (UV–Vis) spectroscopy was employed to evaluate the catalytic performance of the hexapod Ag@AgCl microstructures. The consequences show that the velocity of reaction became faster with a corresponding increase in silver content and the reaction mechanism was cleared. In addition to preparing a good catalyst, this work also promotes the combination of micro-nano materials and spectroscopy technology.Keywords:Ag@AgCl microstructure;in situ monitoring;surface-enhanced Raman spectroscopy;4-nitrothiophenol reduction
危险品化学品经营许可证（带存储）