Effects of Li source on microstructure and ionic conductivity of Al-contained Li6.75La3Zr1.75Ta0.25O12 ceramics
Cubic garnet-type Al-contained Li 6.75 La 3 Zr 1.75 Ta 0.25 O 12 (Al-LLZTO) ceramics were prepared by conventional solid-state reaction using either Li 2 CO 3 or LiOH·H 2 O as Li source. The effects of Li source on the lithium ionic conductivity of Al-LLZTO ceramics were systematically investigated by comparing the synthesis processes and characteristics of the mother powders and the microstructures of the sintered pellets made with different Li sources. Different calcination processes of the raw materials mixtures with different Li sources are revealed by thermogravimetry-differential scanning calorimetry investigation. The mother powder derived from LiOH·H 2 O is of higher sintering activity than those made from Li 2 CO 3 at the same calcination temperature. For the LiOH·H 2 O-derived pellets, higher relative density and enhanced lithium-ion conductivity is achieved at a much lower sintering temperature of 1100 °C as compared with Li 2 CO 3 -derived pellets. The highest conductivity obtained at room temperature is 9.28 × 10 −4 S cm −1 , which is the highest value reported to date for the same Ta doping level.
危险品化学品经营许可证（带存储）