Ethyl acetate is a critical medical indicator for detecting certain types of cancer. However, at present, available sensitive materials often exhibit drawbacks, such as high operating temperatures and poor responses to low concentrations of ethyl acetate. In this study, a ZnO nanorod sensing material was prepared using high-temperature annealing and a hydrothermally synthesized metal-organic framework (MOF) as a template. Au nanodots (AuNDs) were subsequently modified on the ZnO nanorods using an in situ ion reduction, which provided a better dispersion of Au nanodots compared with that obtained using the common reductant method. A variety of characterization methods indicate that the highly dispersed AuNDs, which possess a high catalytic activity, were loaded onto the surface as active centers, leading to a significant augmentation in the adsorption of oxygen on the surface compared with the original ZnO material. Consequently, the AuND@ZnO material exhibited heightened responsiveness to ethyl acetate at a lower operating temperature. The Au@ZnO-based sensor has a response rate (Ra/Rg) of 41.8 to 20 ppm ethyl acetate gas at 140 °C, marking a 17.4-fold increase compared with that of the original material. Due to its low power consumption and high responsiveness, AuND@ZnO is a promising candidate for the detection of ethyl acetate gas in medical applications.
The development of flexible room-temperature gas sensors is important in environmental monitoring and protection. In this contribution, by using 1-octadecanethiol (ODT) as a surface ligand, Au nanodots (NDs) with ultra-small size of ∼1.7 nm were deposited on the surface of α-Fe2O3/reduced graphene oxide (rGO). The Au ND–ODT/α-Fe2O3/rGO composite was fabricated into flexible gas sensors, which could detect NO2 gas down to 200 ppb at room temperature. Compared with α-Fe2O3/rGO, Au ND–ODT/α-Fe2O3/rGO showed enhanced sensing performance because of the beneficial effects of Au NDs, including facilitating the adsorption of NO2 molecules and forming ohmic-like contact with rGO and α-Fe2O3. In addition, the sensing performance of the composite was also influenced by the surface ligands of the Au NDs. Ligands with less polar terminal groups were found to be beneficial to charge transfer in the sensing film. Moreover, Au ND–ODT/α-Fe2O3/rGO-based flexible sensors showed negligible performance deterioration under moderately bent conditions, suggesting their potential to be used in portable and wearable devices.
危险品化学品经营许可证（带存储）