Ultra-low temperature sintered (1–x)BaV2O6-xLiF ceramics for ULTCC and 5 G millimeter-wave antenna applications
(1– x )BaV 2 O 6 - x LiF ( x = 0.025, 0.05, 0.10, 0.15) ceramics with an ultra-low sintering temperature of 475 °C were synthesized using the standard solid-state reaction method. The ceramics demonstrated a remarkable enhancement in the quality factor ( Qf ), reaching a maximum value of 16,800 GHz at x = 0.10, which is 5.6 times higher than that of pure BaV 2 O 6 ceramics obtained in this work. A near-zero temperature coefficient of resonant frequency ( τ f = 1.44 ppm/°C) was simultaneously achieved, together with a dielectric constant ε r of 11.54. Additionally, the chemical compatibility between the present ceramics and the Al electrode was confirmed. Moreover, a millimeter-wave antenna with an excellent S 11 value of −50.3 dB, and a large bandwidth of 3.44 GHz was fabricated using the 0.9BaV 2 O 6 -0.1LiF ceramic as the dielectric resonator . These results highlight the potential application prospects of (1– x )BaV 2 O 6 - x LiF ceramics in the ultra-low temperature co-fired ceramic technology and 5 G millimeter-wave antennas.
危险品化学品经营许可证（带存储）