Hyper-Cross-Linked Resin Modified by a Micropore Polymer for Gas Adsorption and Separation

Chuanhong Wang,Xuefang Chen,Shimiao Yao,Fen Peng,Lian Xiong,Haijun Guo,Hairong Zhang,Xinde Chen

Polymerization confined to the pore was first adapted for the nanoscale structure adjustment of adsorption resin. The self-cross-linked polymer (P-1) formed in the pore of hyper-cross-linked resin (HR) by the Friedel–Crafts reaction of p-dichloroxylene (p-DCX), occupying the macropore of the HR resin and bringing about an external micropore. Compared with the raw HR resin, the volume of the micropore of HR@P-1 in 0.4 < D < 1 nm increased but the volume of the macropore has obviously decreased. After the loading of P-1 in the nanopore of HR, HR@P-1 has better gas adsorption performance. At 298 and 100 KPa, the adsorption capacity of CO2 is almost 30% higher than that of HR, reaching 35.7 cm3/g, due to the increase in the smaller micropore volume. Moreover, HR@P-1 has also been found to be the first C2H6-selective adsorption resin. The uptake of C2H6 is up to 56 cm3/g, and the IAST selectivity of C2H6/CH4 reaches 15.3. HR@P-1 can also separate syngas efficiently at ambient temperature and be regenerated by simple vacuum operation.