Controlling Growth of CuO Nanoparticles on CuFe2O4 Nanotubes and Their Adsorption Kinetics
CuO nanoparticles (NPs) were created in situ on the surface of one-dimensional (1D) CuFe2O4 nanotubes (NTs) by controlling the diffusion of precursors via a two-step synthesis. Fiber precursors were firstly prepared by a single spinneret electrospinning method. A subsequent heat-treatment made the removal of polymers from the precursor fibers. The controlling of molar ratio between Cu and Fe and heating temperature resulted in the morphology change of products. The part of Cu precursors reacted with the Fe precursor to form CuFe2O4 and excess part was diffused to the surface to create CuO NPs. And the density of these NPs could be changed by adjusting the molar ratios of Cu and Fe precursors. CuO NPs were uniformly distributed on the surface of tubular CuFe2O4 fibers using a Cu/Fe molar ratio of 0.65 at 500 °C. Diffusion, nucleation, and growth processes are crucial for the formation and dispersion of CuO NPs. The results of CR adsorption and CO catalytic oxidation indicate that a proper surface structure can play a decisive role in the adsorptive property of the material.
危险品化学品经营许可证（带存储）