In situ formation of D022-Al3Ti during selective laser melting of nano-TiC/AlSi10Mg alloy prepared by electrostatic self-assembly
In this present work, a novel electrostatic self-assembly method was invented to produce AlSi10Mg powders homogeneously decorated with TiC nanoparticles . The TiC/AlSi10Mg alloy with homogenous, crack-free, equiaxed and super fine-grained were produced using selective laser melting (SLM). The in-situ formation of D0 22 -Al 3 Ti created by TiC and Al matrix during SLM was revealed at the first time and both TiC and D0 22 -Al 3 Ti nanoparticles were extremely effective inoculant for an SLMed AlSi10Mg alloy. Therefore, the SLMed TiC/AlSi10Mg alloy exhibited a high tensile strength (ultimate tensile strength ~ 456 MPa, yield strength ~338 MPa) and high microhardness (131 HV 0.05 ), which were higher than the SLMed AlSi10Mg alloy (ultimate tensile strength ~437 MPa, yield strength ~254 MPa and microhardness ~113 HV 0.05 ). This study can be regarded as a guidance in the fabrication of metal matrix nanocomposites using for SLM.