JOURNAL OF THE AMERICAN CERAMIC SOCIETY
·
2024
·
IF 3.5
Xuekai Wang,Yongze Cao,Xianglan Yan,Guojian Li,Xiangping Li,Jinshu Zhang,Baojiu Chen
Hexagonal Er 3+ /Yb 3+ co-doped LaZrTa 3 O 11 (LZTO) phosphor was prepared by molten salt synthesis with B 2 O 3 flux. Holding temperature, holding time, solute and solvent ratio were regulated. The green upconversion luminescence (UCL) integral intensity of the optimal sample can reach 29.2% of β-NaYF 4 :Er 3+ /Yb 3+ under 980 nm laser excitation. This outstanding pure green UCL is due to the low phonon energy, Er 3+ /Yb 3+ monolayer (2D) distribution, asymmetry of Er 3+ /Yb 3+ doped lattice sites, and low oxygen vacancy. The maximum relative temperature sensitivity attains 0.01221 K −1 at 303 K by employing luminescence intensity ratio (LIR) technique. LZTO:Er 3+ /Yb 3+ phosphor can be used in temperature sensing.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
·
2025
·Vol. 36
·期 15
·1-12
·
IF 2.8
Li Meiling,Cao Yongze,Cheng Lihong,Fan Yuhan,Wang Yichao,Li Xiangping,Zhang Xizhen,Chen Baojiu
A series of Er 3+ /Yb 3+ co-doped NaY(WO 4 ) 2 (NYWO) phosphors are prepared by molten salt synthesis (MSS) with Na 2 SO 4 as solvent. The holding temperature, holding time, and solvent-to-solute mass ratio parameters are regulated. The structure, morphology, and luminescence properties of the samples were tested by XRD, SEM, and fluorescence spectrometers, respectively. The lamellar sample is prepared at 900℃ for 5 h when solvent-to-solute is 3, which has the highest pure green upconversion luminescence (UCL) intensity under 980 nm laser excitation. It is demonstrated that the UCL intensity of the samples prepared by MSS is higher than that of solid sintered samples. The maximum absolute sensitivity (S A ) and relative sensitivity (S R ) are 0.012184 K⁻ 1 at 507 K and 0.01102 K⁻ 1 at 303 K, respectively. These materials can be used for pure green luminescence displays and temperature sensing.
研究领域:
材料科学
·
光学
✓ 已验证
DOI
高影响因子
LANGMUIR
·
2022
·
IF 4.331
Peng Du,Laihui Luo,Di Wang,Weiping Li,Dandan Wang,Zhihong Mai,Ye Wang,Weiguang Ran,Guozhong Xing
To settle the unsatisfying efficiency and insufficient light harvesting ability of photocatalysts, we report on the development of Er3+/Yb3+-codoped BiOBr (BiOBr:Er3+/xYb3+) microparticles that were synthesized by a rational high-temperature solid-state reaction method. The prepared microcrystals exhibit high visible upconversion (UC) emissions with maximum intensities at x = 0.01 when excited by a 980 nm laser. Remarkably, the corresponding UC emission process is attributed to a two-photon absorption route. Furthermore, the photocatalytic activities of as-synthesized compounds were further evaluated through analyzing the visible–near-infrared light-triggered tetracycline degradation. Compared with BiOBr:Er3+ microparticles, BiOBr:Er3+/xYb3+ microparticles present superior photocatalytic properties and the optimal status is achieved when x = 0.05, in which h+, ·O2–, and ·OH active species contribute to the photocatalytic mechanism. Additionally, the designed microparticles exhibit better photocatalytic abilities than previously reported photocatalysts (i.e., TiO2, SnO2) upon full-spectrum light irradiation. These results reveal that Yb3+ codoping is able to not only enhance the UC emission properties of BiOBr:Er3+ microparticles but also reinforce their photocatalytic activities. Our findings may put forward a facile strategy to regulate the photodegradation capacity of photcatalysts.
研究领域:
材料科学
·
环境科学
·
光学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
DALTON TRANSACTIONS
·
2022
·Vol. 51
·期 32
·12352-12361
·
IF 4.569
Hongqiang Cui,Yongze Cao,Yuhang Zhang,Lei Li,Guojian Li,Sai Xu,Yichao Wang,Jinsu Zhang,Baojiu Chen
A series of Er3+/Yb3+ co-doped Cs3BiSr(P2O7)2 (CBSPO) phosphors with significant thermal enhancement were successfully prepared using the solid-state method and the thermal-enhancing effect was studied in detail. When the temperature increased from 303 to 723 K, the upconversion luminescence (UCL) emission intensities of 2H11/2 → 4I15/2 and 2H11/2 + 4S3/2 → 4I15/2 of Er3+ in CBSPO:0.1Er3+/0.2Yb3+ were enhanced 22.81 and 10.06 times under 980 nm laser excitation, respectively. Meanwhile, the UCL color of the sample obviously changed from orange to green with the increase in temperature. Furthermore, the UCL thermal enhancement mechanism was demonstrated, which originates from phonon-assisted transitions. In addition, the maximum absolute temperature sensitivity for CBSPO:0.1Er3+/0.2Yb3+ was calculated to be 0.01026 K−1 at 563 K via luminescence intensity ratio (LIR) technology. All the results show that the CBSPO:Er3+/Yb3+ phosphors can be used for safety warning and temperature measurement at high temperatures.
研究领域:
材料科学
·
光学
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2023
·
IF 5.2
Hao Gou,Qian Wu,Laihui Luo,Weiping Li,Peng Du
Series of Er 3+ /Yb 3+ -codoped Gd 2 Mo 3 O 12 (GMO:Er 3+ /2 x Yb 3+ ) microparticles with dual-mode luminescence were fabricated with the assistance of sol-gel method. The phase structure, morphological information, upconversion (UC) and down-shifting luminescence properties of the final products were systematically investigated. At 980 nm light irradiation, strong UC emissions rise in all the products and their intensities depend on the dopant concentration, where the optimum status occurs at x = 0.25 and the two-photon capture procedure results in the UC emission mechanism. Besides, excited at 378 nm, the down-shifting photoluminescence is also gained in resulting samples. By means of the fluorescence intensity ratio technique, the thermometric properties of the studied samples were investigated through analyzing the diverse thermal quenching features of the green emissions from thermally coupled levels of Er 3+ . When the UC emission is selected, the maximum absolute and relative sensitivities of the GMO:Er 3+ /2 x Yb 3+ microparticles are 0.0076 and 1.15% K −1 , respectively, whereas they shift to 0.0036 and 0.89% K −1 , respectively, when the down-shifting photoluminescence is adopted. Note that, the sensor sensitivities of developed microparticles are related to the luminescence mode, while they do not depend on Yb 3+ content. These results suggest that the GMO:Er 3+ /2 x Yb 3+ microparticles are promising thermosensitive luminescent materials for optical thermometry and their thermometric features can be tuned through changing luminescence mode.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF THE OPTICAL SOCIETY OF AMERICA B-OPTICAL PHYSICS
·
2022
·Vol. 39
·期 10
·2625-2636
·
IF 2.058
Hang Liu,Xingke Zheng,Pengcheng Wang,Haiyan Wang,Yuhong Zhang
In this work, a comparative study of the upconversion (UC) luminescence properties of ${{\rm Er}^{3 +}} {-} {{\rm Yb}^{3 +}}$-co-doped ${{\rm AWO}_4}$ (${\rm A} = {\rm Ba}$, Sr, and Ca) scheelite phosphors and ${{\rm Er}^{3 +}} {-} {{\rm Yb}^{3 +}} $-co-doped ${{\rm MgWO}_4}$ wolframite phosphors is reported. Under 980 nm excitation, all the samples emit green and red emissions. The ${{\rm Er}^{3 +}} {-} {{\rm Yb}^{3 +}}$-doped ${{\rm MgWO}_4}$ phosphor has a higher UC emission intensity. Furthermore, the optical temperature sensing properties in ${{\rm Er}^{3 +}} {-} {{\rm Yb}^{3 +}}$-co-doped ${{\rm AWO}_4}$ (${\rm A} = {\rm Ba}$, Sr, Ca, and Mg) phosphor samples are investigated. The relative sensitivity (${{\rm S}_r}$) based on thermally coupled levels (TCLs) increases gradually with an increase in matrix phonon energy. The absolute sensitivity (${{\rm S}_a}$) values of the samples are accurately predicted by the chemical bonding parameter (${{\rm f}_c}$). The results of the correlation between the UC luminescence properties and the microscopic crystal structure, and the relationship of the temperature sensitivity and the host parameters, provide us with a guiding insight for the selection of a host material with ideal temperature measurement capability.
研究领域:
材料科学
·
光学
✓ 已验证
DOI
高影响因子
JOURNAL OF LUMINESCENCE
·
2024
·
IF 3.3
En-Ting Wang,Junhan Yang,Weiping Guo,Qingyi Liu,Qi Zhang,Wei Zhang,Xinhan Chen,Lizhen Zhang,XiaoDong Yi,Guoqiang Wang,Yan Yu,Lingyun Li
Oxychloride phosphors that contain active ions coordinated with both oxygen and chloride ions have garnered significant attention, but the application of oxychloride phosphors is yet limited because of their demanding synthesis condition of vacuum or reducing atmosphere. Herein, we synthesize a new serial oxychlorides of La 9 W 6 O 30 Cl (LWOC) and Er 3+ /Yb 3+ , Ho 3+ /Yb 3+ , Tm 3+ /Yb 3+ doped LWOC through molten salt shielding method (MSS) in air, which is more efficient compared to the traditional method in vacuum. The compound of LWOC crystallizes in the tetragonal system space group P 4 2 / nmc (No. 137) with cell parameters a = b = 10.0445(1) Å, c = 12.6826(4) Å, V = 1279.57(5) Å 3 and Z = 11. The asymmetric unit of LWOC includes three La atoms, one unique W atom, two disordered W atoms with occupancy factors of 0.16(5) and 0.84(5), respectively, one Cl atom and six O atoms. Under the excitation of 980 nm laser, all the Er 3+ /Yb 3+ , Ho 3+ /Yb 3+ and Tm 3+ /Yb 3+ co-doped LWOC phosphors have excellent upconversion (UC) luminescence with bright visible light emission. A fluorescence intensity ratio (FIR) type temperature sensor is developed by using LWOC: Er 3+ , Yb 3+ phosphor as sensing media, which has a maximum relative temperature sensitivity ( S r ) of 0.90 % K −1 at 300 K.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF ALLOYS AND COMPOUNDS
·
2021
·
IF 5.316
Linghui Shen,Tong Wei,Yongchao Shi,Hanyu Hao,Si Chen,Jiaguang Chen,Hao Guan,Qingjun Zhou,Zepeng Li
The various applications of luminescence materials were generally based on the effective modulation of luminescence spectra. However, the research on reversible spectral regulation of up-conversion (UC) luminescence materials was still in its infancy stage. In this work, a class of smart phosphor, Er 3+ and Yb 3+ -codoped SrBi 8 Ti 7 O 27 (SBYT: xEr 3+ ) intergrowth bismuth layer-structured ferroelectric , possessing fast sensitivity to visible light irradiation, was reported based on visible light driven photochromic effect. Through the alternate stimuli of light irradiation and heating treatment, the reversible regulation of UC luminescence was achieved accompanying with the switching of coloration and decoloration processes. The luminescence modulation degree tightly relied on the irradiation time and thermal treatment modes. The reversibility and stability properties were also revealed. Moreover, it is found that polarization treatment was an effective approach which can be adopted to improve the UC luminescence contrast. The maximum luminescence modulation ability of SBYT: xEr 3+ reached up to 81.3% which was 131% of that un-polarized sample. It is believed that SBYT: xEr 3+ ceramics can act as a promising candidate for optical data storage and anti-counterfeiting applications.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
Optical Materials Express
·
2017
·Vol. 7
·期 8
·3003-3010
·
IF 2.591
Hui Li,Yundong Zhang,Lin Shao,ZinMaung Htwe,Pin Yuan
High sensing sensitivity and accuracy is valuable for optical temperature sensors in practical applications. Er3+/Yb3+ co-doped BaZrO3 ceramics were prepared by the dry pressing method. The upconversion luminescence of Er3+/Yb3+ co-doped BaZrO3 ceramics was studied at a temperature range from 300 to 500 K under different pump power. The ratio of non-thermal coupling levels of 4S3/2, 4I9/2→4I15/2 (I546/I875), and 4F9/2, 4I9/2→4I15/2 (I658/I875) show a linear relationship as the temperature increased. The maximum relative sensitivity was estimated to be 1.39% K−1 at 500 K under 90 mW pump power. The result indicated that the BaZrO3:Er3+/Yb3+ ceramic is a promising candidate for high temperature sensing applications.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
MATERIALS RESEARCH BULLETIN
·
2021
·
IF 4.641
Mei-Hong Liu,De-Long Zhang
Er 3+ /Yb 3+ -codoped NaLa(WO 4 ) 2 phosphor samples with different Er 3+ and Yb 3+ doping levels were synthesized by solid-state chemical reaction for optical thermometry and fully characterized. The results show that each phosphor sample mainly consists of NaLa(WO 4 ) 2 crystalline phase and has a nominally stoichiometric chemical composition. The phosphor grains have massive polyhedron morphology, good size homogeneity with a mean value of ∼5 μm and a cutoff phonon energy of 927 cm −1 . The 530 and 550 nm upconversion fluorescence of Er 3+ in the phosphor samples and their temperature characteristics were investigated under 980 nm excitation. The results show that the phosphor exhibits strong upconversion fluorescence and the maximum fluorescence intensity is observed at the optimal Er 3+ and Yb 3+ doping levels of 5 and 20 mol%, respectively. The two-photon process is responsible for the upconversion fluorescence. The spectral structure of either 530 or 550 nm fluorescence band is thermally stable. The peak absolute thermal sensitivity is observed at ∼490 K and has a peak value of ∼9 × 10 -3 K -1 . As expected, Er 3+ or Yb 3+ doping level has little effect on the thermal sensitivity. The phosphor displays a wide dynamical response range of thermal sensitivity from 293 to 800 K, where the sensitivity varies within (6.5–9.0) × 10 -3 K -1 . A comparison study shows that the temperature characteristics obtained from the cooling procedure are almost the same as those obtained from the heating procedure. Besides, the effects of Er 3+ /Yb 3+ doping level and heating/cooling on fluorescence color chromaticity were also studied. Based on the results, the Er 3+ /Yb 3+ -codoped NaLa(WO 4 ) 2 phosphor shows strong fluorescence, good thermal stability, high thermal sensitivity and broad response range of thermal sensitivity. Thus, it is a promising material for thermal detection over a wide temperature range of 293−800 K.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF RARE EARTHS
·
2023
·
IF 4.9
Boxu Xu,Chao Song,Jie Song,Rui Huang,Shaomin Lin,Zhenxu Lin,Yi Zhang,Dejian Hou,Jun Song
In this study, Er 3+ /Yb 3+ codoped Y 2 O 3 –ZnO ceramic phosphors were prepared by sol–gel method. The samples had two emission bands, namely, green (535 nm) and red (660 nm), which are attributed to Er 3+ : 2 H 11/2 ( 4 S 3/2 ) → 4 I 15/2 and Er 3+ : 4 F 9/2 → 4 I 15/2 radiative transitions , respectively. The samples exhibited green- and red-emission intensity enhancement by 1.728 and 2.286 times that of the pure Y 2 O 3 host, respectively and by 514.468 and 214.341 times that of the pure ZnO host. The emission intensities are first enhanced by lattice expansion. With the change of Y:Zn ratio, the high surface energy is converted into low crystal surface resulting in the change of asymmetry crystal field for matrix. When the intensity of the asymmetric crystal field reaches maximum, both emissions are further boosted. When the high surface energy transforms into crystal surface energy, the microstructure changes into a compact mesoporous structure. Consequently, the chemical stability of the samples improves significantly, and the final emission band of the three samples with mesoporous structures is continuously red.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF LUMINESCENCE
·
2025
·
IF 3.6
Xutong Wang,Shuyang Chen,Shiqing Xu,Liang Chen
For the first time, a straightforward optical fiber temperature sensing system based on La 2 MoO 6 :Er 3+ , Yb 3+ phosphors is proposed. The La 2 MoO 6 : Er 3+ , Yb 3+ phosphors were synthesized successfully using the molten salt method. A dual-mode temperature measurement technique based on the fluorescence intensity ratio (FIR) is introduced. The thermally coupled energy levels ( 2 H 11/2 and 4 S 3/2 ) and non-thermally coupled levels ( 2 H 11/2 and 4 F 9/2 ) exhibit maximum relative sensitivities of 1.24 % K −1 and 0.79 % K −1 at 293 K, respectively. The temperature resolution achieved was below 0.5 K. By utilizing the phosphor and optical fiber temperature sensor , real-time and accurate temperature monitoring was achieved, with a temperature deviation of less than 0.5 K. The optical fiber temperature sensor system provides exceptional reversibility and stability, while also playing a crucial role in precise remote temperature measurements under challenging conditions.
研究领域:
材料科学
·
光学工程
·
生物医学传感
·
纳米医学
·
分子影像
✓ 已验证
产品关联
DOI
高影响因子