Liu Yuan-zhen,Xu Qi-yan,Guo Rui-tang,Duan Chao-peng,Wu Gui-lin,Miao Yu-fang,Gu Jing-wen
The Cu/TiO 2 catalysts with the addition of Eu were developed by the sol-gel way for the selective catalytic reduction (SCR) of NO x by NH 3 . Activity tests revealed that CuEu/TiO 2 -0.15 catalyst showed the optimal de-NO x performance in a wide temperature range (150–300 °C), along with an admirable SO 2 tolerance. According to characterization analysis, the relationship between the NH 3 -SCR performance and physicochemical characters of samples was explored. The adjunction of Eu on Cu/TiO 2 catalyst can contribute to the formation of a large amount of Cu 2+ , adsorbed oxygen, and acid sites on the catalyst surface. Moreover, the Eu addition on Cu/TiO 2 is favorable to the generation of activated NO x and NH 3 substances adsorbed on the catalyst surface, which would conduce to the NH 3 -SCR process by Langmuir-Hinshelwood (L-H) mechanism effectively.
Peng Sun,Rui-tang Guo,Shu-ming Liu,Shu-xian Wang,Wei-guo Pan,Ming-yuan Li
A series of MnEuOx catalysts were prepared by the co-precipitation method and used for selective catalytic reduction of NOx with NH 3 . It was found that the modification of MnOx catalyst by Eu with a Eu/Mn molar ratio of 0.1 could greatly enhance its SCR activity and broaden its operating temperature window, accompanied by good resistance to SO 2 and H 2 O. From the characterization results of N 2 adsorption, XRD, XPS, H 2 -TPR, it could be concluded that the larger surface area resulted from the inhibited crystallization of MnOx, the enrichment of surface Mn 4+ and chemisorbed oxygen, and the higher reducibility all made a contribution to the high SCR activity of MnEuOx-0.1 catalyst. Furthermore, the results of in situ DRIFTS study revealed the NH 3 -SCR reactions over MnOx and MnEuOx-0.1 were mainly controlled by L-H mechanism (<150 °C) and E-R mechanism (>150 °C) respectively, and the contribution of E–R mechanism became more important with increasing reaction temperature. The enhanced NO oxidation and NH 3 adsorption should be mainly contribute to the distinguished SCR performance of MnEuOx catalyst in the lower temperature range (<150 °C) and higher temperature range (>150 °C) respectively.
危险品化学品经营许可证（带存储）