Effect of FA+ Fraction and Dipping Time on Performance of FAxMA1−xPbI3 Films and Perovskite Solar Cells
The effects of the formamidinium (FA) + alloy fraction x and the dipping time on the properties of FA x MA 1− x PbI 3 thin films (where MA = methylammonium ) as well as the photovoltaic performance of perovskite solar cells (PSCs) have been studied. Mixed-organic-cation FA x MA 1− x PbI 3 thin films were prepared using a two-step solution deposition method in ambient air. PSCs with fluorine-doped tin oxide glass/compact TiO 2 /mesoporous TiO 2 /FA x MA 1− x PbI 3 /carbon electrode structure were fabricated, aiming to reduce the fabrication costs and improve the stability of PSCs. The results indicated that, when the FA + alloy fraction x was increased from 0 to 1, the x-ray diffraction (XRD) peaks shifted continuously to lower angle, while the absorption edge and photoluminescence (PL) peak shifted continuously towards longer wavelength. The Raman spectra of the FA x MA 1− x PbI 3 thin films, consisting of five typical peaks at 68.5 cm −1 , 77.5 cm −1 , 84.6 cm −1 , 139.1 cm −1 , and 283.2 cm −1 , barely shifted with incorporation of FA + . In addition, the dipping time was shortened by using mixed solvents to prepare the PbI 2 thin films. The PSCs based on FA 0.4 MA 0.6 PbI 3 prepared with a dipping time of 15 min exhibited the highest average power conversion efficiency (PCE) of 8.64%, with 74.4% of the initial efficiency being retained after exposure to ambient air at room temperature with approximately 50% humidity for 700 h.
危险品化学品经营许可证（带存储）