Gold Nanoparticles on Mesoporous SiO2-Coated Magnetic Fe3O4 Spheres: A Magnetically Separatable Catalyst with Good Thermal Stability
Fe3O4spheres with an average size of 273 nm were prepared in the presence of CTAB by a solvothermal method. The spheres were modified by a thin layer of SiO2, and then coated by mesoporous SiO2(m-SiO2) films, by using TEOS as a precursor and CTAB as a soft template. The resulting m-SiO2/Fe3O4spheres, with an average particle size of 320 nm, a high surface area (656 m2/g), and ordered nanopores (average pore size 2.5 nm), were loaded with gold nanoparticles (average size 3.3 nm). The presence of m-SiO2coating could stabilize gold nanoparticles against sintering at 500 °C. The material showed better performance than a conventional Au/SiO2catalyst in catalytic reduction ofp-nitrophenol with NaBH4. It can be separated from the reaction mixture by a magnet and be recycled without obvious loss of catalytic activity. Relevant characterization by XRD, TEM, N2adsorption-desorption, and magnetic measurements were conducted.