Development of Gd-Si-O dispersed 316L stainless steel for improving neutron shielding performance
The low solubility of gadolinium (Gd) limits its application in iron-based neutron shielding alloys. In this study, a high content of Gd up to 7.87 wt.% was added into 316L stainless steel by mechanical alloying (MA) of Gd 2 O 3 with 316L powder. Neutronics calculation results showed that the shielding efficiency of 0.2 mm thick 7.87 wt.% Gd-316L alloy was equivalent to that of 33 mm thick 316L for thermal neutrons. Microstructure analysis indicated that Gd-Si-O particles with an average size of 12.5 nm were uniformly dispersed in the matrix. It revealed that Gd 2 O 3 dissolved into the 316L matrix during MA and re-precipitated at around 780 °C as Gd 2 SiO 5 by XRD and TG-DSC. This study provides a novel Gd-containing alloy designed to achieve integration of structural alloys with good neutron shielding function for future application.