Shishuo Liang,Dong Yang,Jianhua Hu,Shusen Kang,Xue Zhang,Yanchen Fan
With the rapid development of energy storage and electric vehicles, thiophosphate-based all-solid-state batteries (ASSBs) are considered the most promising power source. In order to commercialize ASSBs, the interfacial problem between high-voltage cathode active materials and thiophosphate-based solid-state electrolytes needs to be solved in a simple, effective way. Surface coatings are considered the most promising approach to solving the interfacial problem because surface coatings could prevent direct physical contact between cathode active materials and thiophosphate-based solid-state electrolytes. In this work, Li7La3Zr2O12(LLZO) and LiNbO3(LNO) coatings for LiCoO2(LCO) were fabricated by in-situ interfacial growth of two high-Li+conductive oxide electrolytes on the LCO surface and tested for thiophosphate-based ASSBs. The coatings were obtained from a two-step traditional sol–gel coatings process, the inner coatings were LNO, and the surface coatings were LLZO. Electrochemical evaluations confirmed that the two-layer coatings are beneficial for ASSBs. ASSBs containing LLZO-co-LNO coatings LiCoO2(LLZO&LNO@LCO) significantly improved long-term cycling performance and discharge capacity compared with those assembled from uncoated LCO. LLZO&LNO@LCO||Li6PS5Cl (LPSC)||Li-In delivered discharge capacities of 138.8 mAh/g, 101.8 mAh/g, 60.2 mAh/g, and 40.2 mAh/g at 0.05 C, 0.1 C, 0.2 C, and 0.5 C under room temperature, respectively, and better capacity retentions of 98% after 300 cycles at 0.05 C. The results highlighted promising low-cost and scalable cathode material coatings for ASSBs.Keywords:solid-state batteries;LiCoO2;sulfide solid-state electrolyte;LiNbO3-coating;LLZO-coating
Shouyi Yin,Hongyi Chen,Jun Chen,Abouzar Massoudi,Wentao Deng,Xu Gao,Shu Zhang,Ying Wang,Tsung-Wu Lin,Craig E. Banks,Shi-zhang Qiao,Guoqiang Zou,Hongshuai Hou,Xiaobo Ji
The implementation of Ni-rich cathodes with high energy density has been critically restrained by stress corrosion. Herein, crack-free LiNbO3-coated LiNi0.88Co0.10Mn0.02O2, as theoretically predicted, demonstrates highly reversible lithiation/delithiation. Mechanically, the phase transition (H1 → H2 → H3) is significantly alleviated by the excogitation of the interfacial force invoked by the LiNbO3 coating layer, as verified by X-ray absorption spectroscopy and extended X-ray absorption near-edge structure spectroscopy. Meanwhile, the stabilities of the crystal structure are remarkably strengthened by the strong Nb–O bond activated by Nb5+ doping that is confirmed by Rietveld refinement of X-ray diffraction and differential capacitance curves. Chemically, the interface shielding effect is conducive to protecting the electrode against electrolyte corrosion along with subsequent transition-metal dissolution, ultimately rendering a faster/highly convertible lithium-ion diffusion. Greatly, the excellent electrochemical properties (74% capacity retention after 300 cycles at 2 C within 2.5–4.3 V) and structural stability (the morphology remains intact after 500 cycles at 5 C within 2.5–4.3 V) are successfully achieved. Given this, this elaborate work might inaugurate a potential avenue for rationally tuning the structure/interface evolution toward Ni-rich materials.
危险品化学品经营许可证（带存储）